Browsing by Author "Chaudhry, Muhammed Aslam"

Now showing 1 - 2 of 2
  • Thumbnail Image
    Item
    The kinetics of volatilization from lead glasses
    (Offenbach : Verlag der Deutschen Glastechnischen Gesellschaft, 1975) Cable, Michael; Apak, Can; Chaudhry, Muhammed Aslam
    The diffusion plus surface reaction theory first applied to glass melts by Terai and Ueno is examined and used to Interpret several sets of data by Preston and Turner. First methods of evaluating the reaction rate constant and diffusivity are examined. A simple graphical method is shown to be capable of giving good results in some cases but a sophisticated Computer program is needed in other cases. The theory describes all the data reasonably and the dependence of reaction and diffusivity an temperature and melt composition are evaluated. Most sets of experiments give internally consistent sets of values of the parameters but diffusivity, especially, varies more between different experiments than is reasonable. The true meaning of the diffusivities and reaction rate constants is not clear. Cinétique de la volatilisation à partir de verres au plomb La théorie de la diffusion à laquelle se superpose une reaction en surface, qui avait été appliquée pour la première fois aux fontes de verres par Terai et Ueno, est examinée et utilisée pour interpréter plusieurs séries de données fournies par Preston et Turner. On examine en premier lieu les méthodes permettant d'évaluer la constante de vitesse de reaction et la diffusibilité. On montre qu'une methode graphique simple est susceptible de donner de bons resultats dans ceitains cas mais qu'un programme élaboré de traitement sur crdinateur est requis dans d'autres cas. La théorie décrit toutes les données de faon satisfaisante et les relations liant la reaction et la diffusibilité à la température et à la composition de la fonte sont évaluées. La plupart des séries expérimentales fournissent pour les paramètres des séries de valeurs répondant à une logique interne, bien que la diffusibilité, en particulier, varie de manière moins acceptable au cours des différents essais. La signification reelle des diffusibilités et des constantes de vitesse de reaction n'apparait pas clairement. Zur Kinetik der Verflüchtigung bei Bleigläsern. Die Theorie der Diffusion und Oberflächenreaktion, die zuerst von Terai und Ueno auf Glasschmelzen angewandt wurde, wird überprüft und zur Interpretation einer Reihe von Ergebnissen von Preston und Turner angewandt. Vor allem werden Methoden zur Berechnung der Reaktionsgeschwindigkeitskonstante und des Diffusionskoeffizienten untersucht. Es wird gezeigt, daß eine einfache grafische Methode in einigen Fällen gute Ergebnisse liefert und in anderen ein verfeinertes Rechenprogramm notwendig ist. Die Theorie liefert eine plausible Erklärung für alle Literaturdaten sowie für die festgestellte Abhängigkeit der Reaktion und des Diffusionskoeffizienten von der Temperatur und der Zusammensetzung der Schmelze. Innerhalb der meisten Versuchsreihen ergaben sich jeweils übereinstimmende Werte für die Parameter; zwischen den einzelnen Versuchsreihen variiert aber besonders der Diffusionskoeffizient in einem Umfang, der nicht erklärt werden kann. Die genaue Bedeutung der Diffusionskoeffizienten und der Reaktionsgeschwindigkeitskonstanten ist ungeklärt.
  • Thumbnail Image
    Item
    The kinetics of volatilization of soda from sodium silicate melts
    (Offenbach : Verlag der Deutschen Glastechnischen Gesellschaft, 1975) Cable, Michael; Apak, Can; Chaudhry, Muhammed Aslam
    Data on volatilization loss from 21 compositions in the range 11,8 to 54,8 % Na₂O at temperatures from 1100 to 1400 °C and for times up to 200 h are discussed. The data can be successfully described by a theoretical model which includes diffusion in the melt and a first order reaction at the surface. Values of reaction rate constant (A) are internally consistent in terms of composition and temperature dependence and fall in the range A = 2*10¯⁹ to 2*10¯⁴ cm * s¯¹ . Diffusivity (D) values show considerable scatter and some anomalies in composition and temperature dependence. Many of the anomalous results can be explained by allowing for the strong dependence of D on composition but some results remain difficult to Interpret. Values fall in the range D = 4*10¯¹⁰ to 2*10¯⁸ cm² * s¯¹ . Even after allowing for composition dependence, diffusivities for silica dissolution are about twenty times higher than for volatilization. The true significance of A and D for volatilization remains unclear. Cinétique de la volatilisation d'oxyde de sodium à partir de la fonte de silicate de sodium Les données concernant les pertes par volatilisation obtenues à partir de 21 compositions renfermant de 11,8 à 54,8 % de Na₂O à des températures comprises entre 1100 et 1400 °C et pendant des durées allant jusqu'à 200 h sont discutées. Les données peuvent être décrites de manière satisfaisante en utilisant un modèle théorique qui tient compte de la diffusion dans la fonte et d'une reaction du premier ordre en surface. Les valeurs de la constante de vitesse de réaction A s'accordent bien entre elles en fonction du rapport entre la composition et la température et elles se situent dans le domaine compris entre A = 2*10¯⁹ et A = 2*10¯⁴ cm * s¯¹ . Les valeurs de la diffusibilité D témoignent d'une dispersion importante et de certaines anomalies de la relation température/composition. Bon nombre de ces anomalies peuvent s'expliquer par l'étroite dépendance de D par rapport à la composition; certains resultats restent cependant difficiles à expliquer. Les valeurs se situent entre D = 4*10¯¹⁰ et D = 2*10¯⁸ cm² * s¯¹. Même en tenant compte de la dépendance vis-à-vis de la composition, les diffusibilités correspondant à la dissolution de la silice sont environ vingt fois plus élevées que celles correspondant à la volatilisation. La signification reelle de a et de D dans le cas de la volatilisation reste obscure. Zur Kinetik der Verflüchtigung von Natriumoxid bei Natriumsilicatschmelzen An 21 Natriumsilicatzusammensetzungen mit Na₂O-Gehalten zwischen 11,8 und 54,8 % werden die Verflüchtigungsraten bei Temperaturen zwischen 1100 und 1400 °C und Versuchszeiten bis zu 200 h untersucht. Die Ergebnisse können mit einem theoretischen Modell, das die Diffusion in der Schmelze und eine Reaktion ersten Grades an der Oberfläche berücksichtigt, gut beschrieben werden. Die Werte für die Reaktionsgeschwindigkeitskonstante A sind in Abhängigkeit von der Zusammensetzung und der Temperatur in sich konstant und liegen zwischen 2*10¯⁹ und 2*10¯⁴ cm * s¯¹ . Die Werte für den Diffusionskoeffizienten D weisen eine beträchtliche Streuung sowie einige Anomalitäten in Abhängigkeit von der Zusammensetzung und der Temperatur auf. Viele der anomalen Ergebnisse können mit der großen Abhängigkeit von D von der Zusammensetzung erklärt werden; einige lassen sich eben nur schwer interpretieren. Die Werte für D liegen zwischen 4*10¯¹⁰ und 2*10¯⁸ cm² * s¯¹ . Selbst wenn man die Abhängigkeit von der Zusammensetzung berücksichtigt, sind die Diffusionskoeffizienten der SiO₂-Auflösung etwa 20mal größer als die bei der Verflüchtigung. Die genaue Bedeutung von A und D für den Vorgang der Verflüchtigung bleibt ungeklärt.