Browsing by Author "Gebhardt, Birgitta"

Now showing 1 - 3 of 3
  • Thumbnail Image
    Item
    Corrosion behavior of noble-metal decorations on glass
    (Offenbach : Verlag der Deutschen Glastechnischen Gesellschaft, 1990) Gebhardt, Birgitta
    The finishing of glass surfaces is of increasing economic importance involving beside mechanical strength also chemical durability of the coatings. The decoration of commercial glass might find broader apphcation if it were resistant to the exposure to dishwashing programs. Especially noble-metal decorations are damaged in dishwashing machines for reasons that so far had not been clarified. Important parameters are the composition of the noble-metal preparation, the technique of application, the composition of the base glass, its pretreatment, and, finally, time, temperature and atmosphere in the firing process.
  • Thumbnail Image
    Item
    Mechanical and chemical durability of glass enamels
    (Offenbach : Verlag der Deutschen Glastechnischen Gesellschaft, 1988) Gebhardt, Birgitta; Dannheim, Henning
    The mechanical strength of coated flat glass ("architectural enamel") and the dishwasher durability of household glass decoration were investigated with commercial glasses and enamels. The influence of the composition, the pigment content and the grain size of the enamels as well as the coefficient of thermal expansion, the melting behavior and the surface conditions on chemical and physical properties was shown. The influence of the firing process became obvious at prestressing as well as at firing with longer holding time. The coated samples were investigated as to strain profiles, homogeneity of the layer and crack origins. The strains originating in the enamel were calculated by the three-layer method. After dishwasher treatment and corrosion test, respectively, further parameters like color and gloss were measured. From that concrete proposals resulted for the improvement of the chemical and mechanical resistance of glass enamels.
  • Thumbnail Image
    Item
    Spülmaschinenbeständigkeit von Glas
    (Offenbach : Verlag der Deutschen Glastechnischen Gesellschaft, 1985) Gebhardt, Birgitta
    Es wurden Korrosionsschäden an Glasoberflächen nach Spülmaschinenbehandlung maschinell hergestellter Kelchgläser und mundgeblasener Bechergläser aus Kaliglas untersucht. Das Programm der handelsüblichen Geschirrspülmaschinen entsprach dem vorläufigen Normspülprogramm und wurde bei Temperaturen von 55, 60 und 65 °C bis zu 1000mal durchgeführt. Es zeigten sich zwei typische Schäden nach dem alkalischen Angriff in der Spülmaschine: Schlierenriefen, die nur an maschinell hergestellten Gläsern auftraten, und Mundrandtrübungen, die nur an nachträglich randverwärmten Gläsern erschienen. Die Ursachen für diese Schädigungen, die nur in oberflächennahen Bereichen sowohl außen als auch innen am Glas auftraten, konnten ebenso wie der Verlauf der Schädigung mit zunehmender Behandlungsdauer und -temperatur in der Spülmaschine aufgezeigt werden. Bei den Nachbehandlungsverfahren zur Resistenzerhöhung wurde die Säurepolitur als beste Maßnahme zur Beseitigung der typischen Schäden erkannt. Vorschläge zur Verbesserung der Trübungsresistenz und Verminderung der Neigung, Schlierenriefen zu bilden, wurden im Bereich der Verarbeitungsvorgeschichte der Gläser gemacht.