Browsing by Author "Prager, Lutz"
Now showing 1 - 4 of 4
Results Per Page
- ItemAbschlussbericht zum Teilprojekt "Strahlengehärtete Nanokomposit-Beschichtungen" im Verbundvorhaben "Kratz- und abriebfeste Nanokomposit-Beschichtungen" unter Federführung der DAW Ober-Ramstad(Hannover : Technische Informationsbibliothek (TIB), 2004) Hartmann, Eberhard; Gläsel, Hans-Jürgen; Prager, Lutz[no abstract available]
- ItemFlexible Transparent Barrier Applications of Oxide Thin Films Prepared by Photochemical Conversion at Low Temperature and Ambient Pressure(Lausanne : Frontiers Media, 2020) With, Patrick C.; Helmstedt, Ulrike; Prager, LutzPhotoconversion of metal-organic precursors to thin film metal oxides using ultraviolet (UV) radiation in oxidative atmosphere is an attractive technology because it can be applied at temperatures <80°C and at ambient pressure. Thus, it enables preparing this class of thin films in a cost-efficient manner on temperature sensitive substrates such as polymer films. In this article, various aspects of research and development in the field of photochemical thin-film fabrication, with particular focus to the application of the produced films as gas permeation barriers for the encapsulation of optoelectronic devices are reviewed. Thereby, it covers investigations on fundamental photochemically initiated reactions for precursor classes containing metal-oxygen and metal-nitrogen bonds, and emphazises the relevance of that understanding for applicative considerations like integration of the single-layer barrier films into relevant encapsulation films. Further perspectives are given concerning integration of additional functionalities like electrical conductivity to the flexible and transparent barrier films. © Copyright © 2020 With, Helmstedt and Prager.
- ItemHelium transmission rate as a rapid and reliable method for assessing the water vapour transmission rate of transparent PET-SiOx barrier foils(New York, NY [u.a.] : Wiley, 2021) Herbst, Florian; Großer, Stephan; With, Patrick C.; Prager, Lutz; Pander, MatthiasA single quadrupole mass spectrometer coupled measuring setup was developed for the investigation of the helium transmission rate (HeTR) of SiOx-coated polyethylene terephthalate (PET) barrier films. The setup allows the pressure-less and time-resolved measurements of the helium permeation at transient and steady-state conditions. Whereas standard water vapour transmission rate (WVTR) experiments took extended test times (in the range of several days), HeTR measurements were finished after 1 h. For the material system investigated here, an excellent linear correlation of WVTR and HeTR was proven over two orders of magnitude (regarding WVTR). Experiments with application of different strain loads on the coated films revealed a significant increase of both, HeTR and WVTR. Scanning electron microscope (SEM) measurements evidenced multiple ruptures of the SiOx coating depending on the applied strain and initial thickness of the SiOx layer. Considering virgin barrier films and strain-ruptured barrier films, a good correlation of WVTR and HeTR was shown.
- ItemOberflächenchemie nano- und mikrodimensionaler Materialien und Werkstoffe : Schlussbericht zum Vorhaben ; Laufzeit: 01.09.2008 bis 31.01.2012(Hannover : Technische Informationsbibliothek (TIB), 2012) Rauschenbach, Bernd; Gerlach, Jürgen W.; Hirsch, Dietmar; Mändl, Stephan; Arnold, Th.; Mießler, André; Prager, Lutz; Prager, Andrea; Elsner, Christian; Reichelt, Senta; Pender, Alya[no abstract available]