Browsing by Author "Staněk, Jaroslav"

Now showing 1 - 4 of 4
  • Thumbnail Image
    Item
    Electric glass melting with low-frequency current
    (Offenbach : Verlag der Deutschen Glastechnischen Gesellschaft, 1988) Matěj, Jiří; Staněk, Jaroslav
    Molybdenum electrodes are considerably corroded when melting lead glass by electricity. A theory concerning the corrosion of metal electrodes influenced by alternating current is presented. According to the present knowledge the corrosion increases with decreasing frequency of the alternating current. The new results demonstrate that the dependence of the decrease of electrode radius and of the amount of precipitated lead on frequency exhibits a more complicated course: with decreasing frequency both parameters grow to a maximum, then with further decreasing frequency they decrease to a minimum, which may be lower than the value corresponding to the zero current loading of the electrode. Only at very low frequency the corrosion grows again. An explanation of this behaviour is given. This new knowledge may be used to suppress the corrosion processes which occur in the electric melting of lead glass in a furnace equipped with molybdenum electrodes. A frequency converter for converting the main frequency into a required lower one, as well as the results of several years application of this method to the melting of 24 % PbO crystal glass in a furnace with a capacity of 12 t glass/d are described.
  • Thumbnail Image
    Item
    Messung der Enthalpie und Berechnung der spezifischen Wärme von Glas
    (Offenbach : Verlag der Deutschen Glastechnischen Gesellschaft, 1972) Tydlitát, Vratislav; Blažek, Antonin; Endrýs, Jiři; Staněk, Jaroslav
    Die mittlere spezifische Wärme von Gläsern wurde experimentell und rechnerisch bestimmt. Für die Versuche wurde ein Mischungskalorimeter verwendet. Ein Vergleich der gemessenen und rechnerisch bestimmten Werte von c̅p zeigt eine relativ gute Übereinstimmung. Die experimentell ermittelten Ergebnisse werden mit den Werten der wahren spezifischen Wärme bei hohen Temperaturen verglichen, die mit Hilfe der Theorie der Schwingungswärme von Atomen berechnet worden sind.
  • Thumbnail Image
    Item
    Strahlungswärmeleitfähigkeit von Glas Einfluß der Glaszusammensetzung auf seine Wärmedurchlässigkeit
    (Offenbach : Verlag der Deutschen Glastechnischen Gesellschaft, 1976) Blažek, Antonín; Endrýs, Jiří; Kada, Josef; Staněk, Jaroslav
    Es wird eine Methode zur Bestimmung der Wärmeleitfähigkeit von Glasschmelzen beschrieben, die auf der Bestimmung der Absorptionseigenschaften des Glases im nahen infraroten Gebiet und auf Berechnung der Wärmeleitfähigkeit (kr) auf Grund von theoretisch abgeleiteten Gleichungen beruht. Die Strahlungsdurchlässigkeit des Glases wurde dabei im Temperaturbereich von 20 bis 1400° C und im Wellenlängengebiet von 0,5 bis 4,75 µm gemessen. Der Einfluß der chemischen Zusammensetzung auf die Wärmeleitfähigkeit wurde bei elf Weißgläsern untersucht und mathematisch formuliert. Der wesentliche Einfluß von Fe₂O₃ auf die Wärmedurchlässigkeit der Glasschmelze konnte nachgewiesen werden. Thermal radiation conductivity of glass — influence of glass composition on its heat transmission — A method of determining the thermal conductivity of glass melts has been described. This is based on the determination of absorption properties in the near infrared and calculations based on theoretically derived equations. The transmissivity of glass has been measured from 0,5 to 4,75µm between 20 and 1400° C. The influence of glass composition on thermal conductivity has been investigated and formulated mathematically using results for 11 colourless glasses. The important influence of the Fe₂O₃ content on the heat transmission can be established. Conductibilité thermique par rayonnement du verre Influence de la composition du verre sur sa conductibilité thermique — On décrit une methode de détermination de la conduc-tibilité thermique d'une fonte de verre basée sur la déter-mination des propriétés d'absorption du verre dans l'infra-rouge proche et sur le calcul de la conductibilité thermique (kr) au moyen des equations dérivées théoriquement. La transmission de rayonnement du verre est alors mesurée dans le domaine de températures de 20 à 1400 °C et dans le domaine de longueurs d'ondes de 0,5 à 4,75µm. L'influence de la composition chimique sur la conductibilité thermique est étudiée dans 11 verres blancs et est formulée mathématique-ment. L'influence prépondérante de Fe₂O₃ sur la conduc-tibilité thermique de la fonte de verre a pu être mise en évidence.
  • Thumbnail Image
    Item
    Untersuchungen über den Polierprozeß von Glas Teil IV. Oberflächenfehler beim Polieren mit gebundenem Korn
    (Offenbach : Verlag der Deutschen Glastechnischen Gesellschaft, 1967) Götz, Jiří; Staněk, Jaroslav
    Im letzten Teil der Untersuchungen über den Polierprozeß von Glas werden zwei besondere Arten von Oberflächendefekten beschrieben, die nur beim Polieren mit gebundenem Korn beobachtet werden können. Die Defekte der ersten Gruppe entstehen beim Anpolieren der Glasoberfläche unter einem scharfen Winkel; die Glasoberfläche ist hierbei durch Stoffverschiebungseffekte gekennzeichnet. Flächenhafte Dilatationssprünge in der bearbeiteten Glasoberfläche entstehen infolge sehr hoher Kontakttemperaturen zwischen Glasoberfläche und Polierinstrument. Beide Oberflächenfehler können durch Änderung der technologischen Parameter des Polierprozesses beseitigt werden.