Spectrophotometric analysis of ferrous, ferric and total iron content in soda-lime-silica glass

Abstract

A study of the bands of charge transfer and of d-d transition was performed in view of quantitative analysis of ferrous, ferric and total iron content. For a given wavelength between 0.32 und 0.33 μm a linear relationship between the absorption and the total iron content can be found for all the redox states studied. Using the band at 1.06 μm allows [Fe2+] determination and by means of the band at 0.38 μm [Fe3+] can also be measured accurately if correction is made using the total iron content. The results of spectroscopic determinations are shown to be coherent with those of chemical analysis to within 1 to 3 %. Eine Untersuchung der Banden der Ladungsübertragung und des d-d-Übergange s wurde mit dem Ziel einer quantitativen Analyse des Fe2+-, Fe3+- und Gesamteisengehaltes durchgeführt. Für eine gegebene Wellenlänge zwischen 0,32 und 0,33 μm kann für alle untersuchten Redoxzustände eine lineare Beziehung zwischen der Absorption und dem Gesamteisengehalt gefunden werden. Die Verwendung der Bande bei 1,06 μm erlaubt die Bestimmung der Fe2+-Konzentration. Mit Hilfe der Bande bei 0,38 μm kann auch der Fe3+-Gehalt genau ermittelt werden, wenn eine Korrektur unter Anwendung des Gesamteisengehaltes durchgeführt wurde. Es konnte gezeigt werden, daß spektroskopische Messungen und chemische Analysen innerhalb von 1 bis 3 % übereinstimmen.