Microstructure and magnetic character of terbium borate glass

Abstract

Microstructure and magnetic character of 30 Tb2O3 · 70 B2O3 glass have been examined by means of high-resolution transmission electron microscopy and magnetization measurements. Although no trace of crystahine phases was observed in the electron diffraction pattern, the transmission electron micrograph revealed that there exist clusters, the size of which is about 1 nm, in the present glass. The magnetization measurements showed that this glass is paramagnetic at room temperature. However, the magnetization is high enough for the glass to adhere to a permanent magnet in the Nd-Fe-B system at room temperature. Mikrostruktur und magnetisches Verhalten eines 30 Tb2O3 · 70 B2O3-Glases wurden mit Hilfe hochauflösender Elektronentransmissionsmikroskopie und Magnetisierungsmessungen untersucht. Obwohl kein Anzeichen von kristallinen Phasen in dem Elektronenbeugungsbild beobachtet wird, zeigt das Gefügebild der Durchstrahlungselektronenmikroskopie, daß in dem untersuchten Glas Nester existieren, deren Größe etwa 1 nm ist. Die Magnetisierungsmessungen zeigten, daß dieses Glas bei Raumtemperatur paramagnetisch ist. Die Magnetisierung ist jedoch für das Glas hoch genug, daß es bei Raumtemperatur an dem Dauermagneten des Systems Nd-Fe-B haften bleibt.