Nucleation in a precursor glass for a Li2O-Al2O3-SiO2 glass ceramic Part 2. Variation of the nucleating agent concentrations

Abstract

The influence of nucleating oxide concentration on nucleation in a parent glass of a Li2O-Al2O3-SiO2 glass ceramic is investigated by means of a method described in part 1 of this paper. Furthermore it is investigated to which extent glasses with different concentrations of nucleating agents can be transformed into useable glass ceramics. It is shown that with decreasing concentration of the nucleating agents the nucleation process is slowed down. The data present a basis for improved processing. The study of properties of ceramized glasses with varied concentration of nucleating agents clearly indicates that a reduction in the nucleation tendency can be counteracted by changing the nucleation conditions during ceramizing. An einem Ausgangsglas einer Li2O-Al2O3-SiO2-Glaskeramik wird mit Hilfe der in Teil 1 dieser Arbeit beschriebenen Keimentwicklungsmethode der Einfluß von Veränderungen der Konzentration der Keimbildneroxide auf die Keimbildung untersucht. Weiterhin wird geprüft, inwieweit sich die Gläser mit veränderten Keimbildnergehalten in brauchbare Glaskeramiken umwandeln lassen. Es zeigt sich, daß die Konzentrationsverringerung jewehs eines Keimbildners zu einer Verlangsamung des Keimbildungsprozesses führt. Dies schafft die Voraussetzungen für eine bessere Verarbeitbarkeit der Gläser. An Hand von Eigenschaftsuntersuchungen der keramisierten, keimbildnervariierten Gläser wird deutlich, daß eine Reduzierung des Keimbildungsvermögens in gewissen Grenzen durch veränderte Keimbildungsbedingungen während der Keramisierung ausgeglichen werden kann.