European pressed glass 1986 to 1990

Abstract

On the basis of the analyses of 37 samples of pressed soda-lime glass from the years 1986 to 1990, manufactured in European countries, the average composition of the glass from single manufacturers as well as the total average composition has been determined. The results were compared with similar statistical data from the years 1970 to 1985. The result shows that the glass composition for ordinary pressed glass products has the orientation to be simpler, with less "additional oxides", and it is tending to become similar to that of container glass, with the only difference being in a lower iron and a higher alkali content. Nevertheless, the composition of the samples corresponds only vaguely with that of standard crystal glass. An Hand von Analysen an 37 Kalk-Natron-Preßgläsern aus europäischer Produktion der Jahre 1986 bis 1990 werden die durchschnittliche Zusammensetzung der Gläser einzelner Hersteller sowie der Gesamtdurchschnitt der Glaszusammensetzungen aller Hersteller ermittelt. Die Ergebnisse werden mit ähnlichen statistischen Daten aus den Jahren 1970 bis 1985 verglichen. Daraus ergibt sich die Tendenz, daß die Glaszusammensetzung für gewöhnliche Preßglasprodukte einfacher geworden ist, weniger zusätzliche Oxide enthält und der Zusammensetzung von Behälterglas nahekommt. Der einzige Unterschied besteht im niedrigeren Eisen- und höheren Alkaligehalt. Dennoch entspricht die Zusammensetzung nur ungefähr der des Standardkristallglases.