Browsing by Author "Liao, Zhongquan"
Now showing 1 - 6 of 6
Results Per Page
Sort Options
- ItemInterfacial Covalent Bonds Regulated Electron-Deficient 2D Black Phosphorus for Electrocatalytic Oxygen Reactions(Weinheim : Wiley-VCH, 2021) Wang, Xia; Raghupathy, Ramya Kormath Madam; Querebillo, Christine Joy; Liao, Zhongquan; Li, Dongqi; Lin, Kui; Hantusch, Martin; Sofer, Zdeněk; Li, Baohua; Zschech, Ehrenfried; Weidinger, Inez M.; Kühne, Thomas D.; Mirhosseini, Hossein; Yu, Minghao; Feng, XinliangDeveloping resource-abundant and sustainable metal-free bifunctional oxygen electrocatalysts is essential for the practical application of zinc–air batteries (ZABs). 2D black phosphorus (BP) with fully exposed atoms and active lone pair electrons can be promising for oxygen electrocatalysts, which, however, suffers from low catalytic activity and poor electrochemical stability. Herein, guided by density functional theory (DFT) calculations, an efficient metal-free electrocatalyst is demonstrated via covalently bonding BP nanosheets with graphitic carbon nitride (denoted BP-CN-c). The polarized P-N covalent bonds in BP-CN-c can efficiently regulate the electron transfer from BP to graphitic carbon nitride and significantly promote the OOH* adsorption on phosphorus atoms. Impressively, the oxygen evolution reaction performance of BP-CN-c (overpotential of 350 mV at 10 mA cm−2, 90% retention after 10 h operation) represents the state-of-the-art among the reported BP-based metal-free catalysts. Additionally, BP-CN-c exhibits a small half-wave overpotential of 390 mV for oxygen reduction reaction, representing the first bifunctional BP-based metal-free oxygen catalyst. Moreover, ZABs are assembled incorporating BP-CN-c cathodes, delivering a substantially higher peak power density (168.3 mW cm−2) than the Pt/C+RuO2-based ZABs (101.3 mW cm−2). The acquired insights into interfacial covalent bonds pave the way for the rational design of new and affordable metal-free catalysts. © 2021 The Authors. Advanced Materials published by Wiley-VCH GmbH
- ItemNitrogen and boron doped carbon layer coated multiwall carbon nanotubes as high performance anode materials for lithium ion batteries([London] : Nature Publishing Group, 2021) Liu, Bo; Sun, Xiaolei; Liao, Zhongquan; Lu, Xueyi; Zhang, Lin; Hao, Guang-PingLithium ion batteries (LIBs) are at present widely used as energy storage and conversion device in our daily life. However, due to the limited power density, the application of LIBs is still restricted in some areas such as commercial vehicles or heavy-duty trucks. An effective strategy to solve this problem is to increase energy density through the development of battery materials. At the same time, a stable long cycling battery is a great demand of environmental protection and industry. Herein we present our new materials, nitrogen and boron doped carbon layer coated multiwall carbon nanotubes (NBC@MWCNTs), which can be used as anodes for LIBs. The electrochemical results demonstrate that the designed NBC@MWCNTs electrode possesses high stable capacity over an ultra-long cycling lifespan (5000 cycles) and superior rate capability even at very high current density (67.5 A g−1). Such impressive lithium storage properties could be ascribed to the synergistic coupling effect of the distinctive structural features, the reduced diffusion length of lithium ions, more active sites generated by doped atoms for lithium storage, as well as the enhancement of the electrode structural integrity. Taken together, these results indicate that the N, B-doped carbon@MWCNTs materials may have great potential for applications in next-generation high performance rechargeable batteries.
- ItemPolymerization driven monomer passage through monolayer chemical vapour deposition graphene([London] : Nature Publishing Group UK, 2018-10-3) Zhang, Tao; Liao, Zhongquan; Sandonas, Leonardo Medrano; Dianat, Arezoo; Liu, Xiaoling; Xiao, Peng; Amin, Ihsan; Gutierrez, Rafael; Chen, Tao; Zschech, Ehrenfried; Cuniberti, Gianaurelio; Jordan, RainerMass transport through graphene is receiving increasing attention due to the potential for molecular sieving. Experimental studies are mostly limited to the translocation of protons, ions, and water molecules, and results for larger molecules through graphene are rare. Here, we perform controlled radical polymerization with surface-anchored self-assembled initiator monolayer in a monomer solution with single-layer graphene separating the initiator from the monomer. We demonstrate that neutral monomers are able to pass through the graphene (via native defects) and increase the graphene defects ratio (Raman ID/IG) from ca. 0.09 to 0.22. The translocations of anionic and cationic monomers through graphene are significantly slower due to chemical interactions of monomers with the graphene defects. Interestingly, if micropatterned initiator-monolayers are used, the translocations of anionic monomers apparently cut the graphene sheet into congruent microscopic structures. The varied interactions between monomers and graphene defects are further investigated by quantum molecular dynamics simulations.
- ItemTwo-Dimensional Boronate Ester Covalent Organic Framework Thin Films with Large Single Crystalline Domains for a Neuromorphic Memory Device(Weinheim : Wiley-VCH, 2020) Park, SangWook; Liao, Zhongquan; Ibarlucea, Bergoi; Qi, Haoyuan; Lin, Hung-Hsuan; Becker, Daniel; Melidonie, Jason; Zhang, Tao; Sahabudeen, Hafeesudeen; Baraban, Larysa; Baek, Chang-Ki; Zheng, Zhikun; Zschech, Ehrenfried; Fery, Andreas; Heine, Thomas; Kaiser, Ute; Cuniberti, Gianaurelio; Dong, Renhao; Feng, XinliangDespite the recent progress in the synthesis of crystalline boronate ester covalent organic frameworks (BECOFs) in powder and thin-film through solvothermal method and on-solid-surface synthesis, respectively, their applications in electronics, remain less explored due to the challenges in thin-film processability and device integration associated with the control of film thickness, layer orientation, stability and crystallinity. Moreover, although the crystalline domain sizes of the powder samples can reach micrometer scale (up to ≈1.5 μm), the reported thin-film samples have so far rather small crystalline domains up to 100 nm. Here we demonstrate a general and efficient synthesis of crystalline two-dimensional (2D) BECOF films composed of porphyrin macrocycles and phenyl or naphthyl linkers (named as 2D BECOF-PP or 2D BECOF-PN) by employing a surfactant-monolayer-assisted interfacial synthesis (SMAIS) on the water surface. The achieved 2D BECOF-PP is featured as free-standing thin film with large single-crystalline domains up to ≈60 μm2 and tunable thickness from 6 to 16 nm. A hybrid memory device composed of 2D BECOF-PP film on silicon nanowire-based field-effect transistor is demonstrated as a bio-inspired system to mimic neuronal synapses, displaying a learning–erasing–forgetting memory process. © 2020 The Authors. Published by Wiley-VCH Verlag GmbH & Co. KGaA.
- ItemUltrathin positively charged electrode skin for durable anion-intercalation battery chemistries([London] : Nature Publishing Group UK, 2023) Sabaghi, Davood; Wang, Zhiyong; Bhauriyal, Preeti; Lu, Qiongqiong; Morag, Ahiud; Mikhailovia, Daria; Hashemi, Payam; Li, Dongqi; Neumann, Christof; Liao, Zhongquan; Dominic, Anna Maria; Nia, Ali Shaygan; Dong, Renhao; Zschech, Ehrenfried; Turchanin, Andrey; Heine, Thomas; Yu, Minghao; Feng, XinliangThe anion-intercalation chemistries of graphite have the potential to construct batteries with promising energy and power breakthroughs. Here, we report the use of an ultrathin, positively charged two-dimensional poly(pyridinium salt) membrane (C2DP) as the graphite electrode skin to overcome the critical durability problem. Large-area C2DP enables the conformal coating on the graphite electrode, remarkably alleviating the electrolyte. Meanwhile, the dense face-on oriented single crystals with ultrathin thickness and cationic backbones allow C2DP with high anion-transport capability and selectivity. Such desirable anion-transport properties of C2DP prevent the cation/solvent co-intercalation into the graphite electrode and suppress the consequent structure collapse. An impressive PF6−-intercalation durability is demonstrated for the C2DP-covered graphite electrode, with capacity retention of 92.8% after 1000 cycles at 1 C and Coulombic efficiencies of > 99%. The feasibility of constructing artificial ion-regulating electrode skins with precisely customized two-dimensional polymers offers viable means to promote problematic battery chemistries.
- ItemUltrathin positively charged electrode skin for durable anion-intercalation battery chemistries([London] : Nature Publishing Group UK, 2023) Sabaghi, Davood; Wang, Zhiyong; Bhauriyal, Preeti; Lu, Qiongqiong; Morag, Ahiud; Mikhailovia, Daria; Hashemi, Payam; Li, Dongqi; Neumann, Christof; Liao, Zhongquan; Dominic, Anna Maria; Nia, Ali Shaygan; Dong, Renhao; Zschech, Ehrenfried; Turchanin, Andrey; Heine, Thomas; Yu, Minghao; Feng, XinliangThe anion-intercalation chemistries of graphite have the potential to construct batteries with promising energy and power breakthroughs. Here, we report the use of an ultrathin, positively charged two-dimensional poly(pyridinium salt) membrane (C2DP) as the graphite electrode skin to overcome the critical durability problem. Large-area C2DP enables the conformal coating on the graphite electrode, remarkably alleviating the electrolyte. Meanwhile, the dense face-on oriented single crystals with ultrathin thickness and cationic backbones allow C2DP with high anion-transport capability and selectivity. Such desirable anion-transport properties of C2DP prevent the cation/solvent co-intercalation into the graphite electrode and suppress the consequent structure collapse. An impressive PF6−-intercalation durability is demonstrated for the C2DP-covered graphite electrode, with capacity retention of 92.8% after 1000 cycles at 1 C and Coulombic efficiencies of > 99%. The feasibility of constructing artificial ion-regulating electrode skins with precisely customized two-dimensional polymers offers viable means to promote problematic battery chemistries.