3 results
Search Results
Now showing 1 - 3 of 3
- ItemMicrostructure, Texture, and Strength Development during High-Pressure Torsion of CrMnFeCoNi High-Entropy Alloy(Basel : MDPI, 2020) Skrotzki, Werner; Pukenas, Aurimas; Odor, Eva; Joni, Bertalan; Ungar, Tamas; Völker, Bernhard; Hohenwarter, Anton; Pippan, Reinhard; George, Easo P.The equiatomic face-centered cubic high-entropy alloy CrMnFeCoNi was severely deformed at room and liquid nitrogen temperature by high-pressure torsion up to shear strains of about 170. Itsmicrostructurewas analyzed by X-ray line profile analysis and transmission electronmicroscopy and its texture by X-ray microdiffraction. Microhardness measurements, after severe plastic deformation, were done at room temperature. It is shown that at a shear strain of about 20, a steady state grain size of 24 nm, and a dislocation density of the order of 1016 m-2 is reached. The dislocations are mainly screw-type with low dipole character. Mechanical twinning at room temperature is replaced by a martensitic phase transformation at 77 K. The texture developed at room temperature is typical for sheared face-centered cubic nanocrystalline metals, but it is extremely weak and becomes almost random after high-pressure torsion at 77 K. The strength of the nanocrystalline material produced by high-pressure torsion at 77 K is lower than that produced at room temperature. The results are discussed in terms of different mechanisms of deformation, including dislocation generation and propagation, twinning, grain boundary sliding, and phase transformation. © 2020 by the authors. Licensee MDPI, Basel, Switzerland.
- ItemPhase Transformation Induced by High Pressure Torsion in the High-Entropy Alloy CrMnFeCoNi(Basel : MDPI, 2022) Chulist, Robert; Pukenas, Aurimas; Chekhonin, Paul; Hohenwarter, Anton; Pippan, Reinhard; Schell, Norbert; Skrotzki, WernerThe forward and reverse phase transformation from face-centered cubic (fcc) to hexagonal close-packed (hcp) in the equiatomic high-entropy alloy (HEA) CrMnFeCoNi has been investigated with diffraction of high-energy synchrotron radiation. The forward transformation has been induced by high pressure torsion at room and liquid nitrogen temperature by applying different hydrostatic pressures and large shear strains. The volume fraction of hcp phase has been determined by Rietveld analysis after pressure release and heating-up to room temperature as a function of hydrostatic pressure. It increases with pressure and decreasing temperature. Depending on temperature, a certain pressure is necessary to induce the phase transformation. In addition, the onset pressure depends on hydrostaticity; it is lowered by shear stresses. The reverse transformation evolves over a long period of time at ambient conditions due to the destabilization of the hcp phase. The effect of the phase transformation on the microstructure and texture development and corresponding microhardness of the HEA at room temperature is demonstrated. The phase transformation leads to an inhomogeneous microstructure, weakening of the shear texture, and a surprising hardness anomaly. Reasons for the hardness anomaly are discussed in detail.
- ItemHigh strength nanocrystalline Cu–Co alloys with high tensile ductility(Cambridge : Cambridge University Press, 2018) Bachmaier, Andrea; Rathmayr, Georg Benedikt; Schmauch, Jörg; Schell, Norbert; Stark, Andreas; de Jonge, Niels; Pippan, ReinhardA supersaturated single-phase Cu–26 at.% Co alloy was produced by high-pressure torsion deformation, leading to a nanocrystalline microstructure with a grain size smaller than 100 nm. The nonequilibrium solid solution decomposed during subsequent isothermal annealing. In situ high-energy X-ray diffraction was used to map changes linked to the separating phases, and the development of a nanoscale Cu–Co composite structure was observed. To gain further information about the relationship of the microstructure and the mechanical properties after phase separation, uniaxial tensile tests were conducted on as-deformed and isothermally annealed samples. Based on the in situ diffraction data, different isothermal annealing temperatures were chosen. Miniaturized tensile specimens with a round cross section were tested, and an image-based data evaluation method enabled the evaluation of true stress–strain curves and strain hardening behavior. The main results are as follows: all microstructural states showed high strength and ductility, which was achieved by a combination of strain-hardening and strain-rate hardening.