7 results
Search Results
Now showing 1 - 7 of 7
- ItemHigh-temperature annealing of AlN films grown on 4H-SiC(New York, NY : American Inst. of Physics, 2020) Brunner, F.; Cancellara, L.; Hagedorn, S.; Albrecht, M.; Weyers, M.The effect of high-temperature annealing (HTA) at 1700 °C on AlN films grown on 4H-SiC substrates by metalorganic vapor phase epitaxy has been studied. It is shown that the structural quality of the AlN layers improves significantly after HTA similar to what has been demonstrated for AlN grown on sapphire. Dislocation densities reduce by one order of magnitude resulting in 8 × 108 cm-2 for a-type and 1 × 108 cm-2 for c-type dislocations. The high-temperature treatment removes pits from the surface by dissolving nanotubes and dislocations in the material. XRD measurements prove that the residual strain in AlN/4H-SiC is further relaxed after annealing. AlN films grown at higher temperature resulting in a lower as-grown defect density show only a marginal reduction in dislocation density after annealing. Secondary ion mass spectrometry investigation of impurity concentrations reveals an increase of Si after HTA probably due to in-diffusion from the SiC substrate. However, C concentration reduces considerably with HTA that points to an efficient carbon removal process (i.e., CO formation). © 2020 Author(s).
- ItemGrowth and Properties of Intentionally Carbon-Doped GaN Layers(Weinheim : Wiley-VCH, 2019) Richter, Eberhard; Beyer, Franziska C.; Zimmermann, Friederike; Gärtner, Günter; Irmscher, Klaus; Gamov, Ivan; Heitmann, Johannes; Weyers, Markus; Tränkle, GüntherCarbon-doping of GaN layers with thickness in the mm-range is performed by hydride vapor phase epitaxy. Characterization by optical and electrical measurements reveals semi-insulating behavior with a maximum of specific resistivity of 2 × 1010 Ω cm at room temperature found for a carbon concentration of 8.8 × 1018 cm−3. For higher carbon levels up to 3.5 × 1019 cm−3, a slight increase of the conductivity is observed and related to self-compensation and passivation of the acceptor. The acceptor can be identified as CN with an electrical activation energy of 0.94 eV and partial passivation by interstitial hydrogen. In addition, two differently oriented tri-carbon defects, CN-a-CGa-a-CN and CN-a-CGa-c-CN, are identified which probably compensate about two-thirds of the carbon which is incorporated in excess of 2 × 1018 cm−3. © 2019 The Authors. Published by WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
- ItemHigh‐Temperature Annealing and Patterned AlN/Sapphire Interfaces(Weinheim : Wiley-VCH, 2021) Hagedorn, Sylvia; Mogilatenko, Anna; Walde, Sebastian; Pacak, Daniel; Weinrich, Jonas; Hartmann, Carsten; Weyers, MarkusUsing the example of epitaxial lateral overgrowth of AlN on trench-patterned AlN/sapphire templates, the impact of introducing a high-temperature annealing step into the process chain is investigated. Covering the open surfaces of sapphire trench sidewalls with a thin layer of AlN is found to be necessary to preserve the trench shape during annealing. Both the influence of annealing temperature and annealing duration are investigated. To avoid the deformation of the AlN/sapphire interface during annealing, the annealing duration or annealing temperature must be low enough. Annealing for 1 h at 1730 °C is found to allow for the lowest threading dislocation density of 3.5 × 108 cm−2 in the subsequently grown AlN, while maintaining an uncracked smooth surface over the entire 2 in. wafer. Transmission electron microscopy study confirms the defect reduction by high-temperature annealing and reveals an additional strain relaxation mechanism by accumulation of horizontal dislocation lines at the interface between annealed and nonannealed AlN. By applying a second annealing step, the dislocation density can be further reduced to 2.5 × 108 cm−2.
- ItemCurrent Status of Carbon‐Related Defect Luminescence in GaN(Weinheim : Wiley-VCH, 2021) Zimmermann, Friederike; Beyer, Jan; Röder, Christian; Beyer, Franziska C.; Richter, Eberhard; Irmscher, Klaus; Heitmann, JohannesHighly insulating layers are a prerequisite for gallium nitride (GaN)-based power electronic devices. For this purpose, carbon doping is one of the currently pursued approaches. However, its impact on the optical and electrical properties of GaN has been widely debated in the scientific community. For further improvement of device performance, a better understanding of the role of related defects is essential. To study optically active point defects, photoluminescence is one of the most frequently used experimental characterization techniques. Herein, the main recent advances in the attribution of carbon-related photoluminescence bands are reviewed, which were enabled by the interplay of a refinement of growth and characterization techniques and state-of-the-art first-principles calculations developed during the last decade. The predicted electronic structures of isolated carbon defects and selected carbon-impurity complexes are compared to experimental results. Taking into account both of these, a comprehensive overview on the present state of interpretation of carbon-related broad luminescence bands in bulk GaN is presented.
- ItemHigh-Temperature Annealing of AlGaN(Weinheim : Wiley-VCH, 2020) Hagedorn, Sylvia; Khan, Taimoor; Netzel, Carsten; Hartmann, Carsten; Walde, Sebastian; Weyers, MarkusIn the past few years, high-temperature annealing of AlN has become a proven method for providing AlN layers with low dislocation densities. Herein, the example of Al0.77Ga0.23N is used to investigate whether annealing can also improve the material quality of the ternary alloy. A detailed analysis of the influence of annealing temperature on structural and optical material properties is presented. It is found that with increasing annealing temperature, the threading dislocation density can be lowered from an initial value of 6.0 × 109 down to 2.6 × 109 cm−2. Ga depletion at the AlGaN surface and Ga diffusion into the AlN buffer layer are observed. After annealing, the defect luminescence between 3 and 4 eV is increased, accompanied by an increase in the oxygen concentration by about two orders of magnitude. Furthermore, due to annealing optical absorption at 325 nm (3.8 eV) occurs, which increases with increasing annealing temperature. It is assumed that the reason for this decrease in ultraviolet (UV) transmittance is the increasing number of vacancies caused by the removal of group-III and N atoms from the AlGaN lattice during annealing.
- ItemSuppression of particle formation by gas-phase pre-reactions in (100) MOVPE-grown β -Ga2O3films for vertical device application(Melville, NY : American Inst. of Physics, 2023) Chou, Ta-Shun; Seyidov, Palvan; Bin Anooz, Saud; Grüneberg, Raimund; Pietsch, Mike; Rehm, Jana; Tran, Thi Thuy Vi; Tetzner, Kornelius; Galazka, Zbigniew; Albrecht, Martin; Irmscher, Klaus; Fiedler, Andreas; Popp, AndreasThis work investigated the metalorganic vapor-phase epitaxy (MOVPE) of (100) β-Ga2O3 films with the aim of meeting the requirements to act as drift layers for high-power electronic devices. A height-adjustable showerhead achieving a close distance to the susceptor (1.5 cm) was demonstrated to be a critical factor in increasing the stability of the Ga wetting layer (or Ga adlayer) on the surface and reducing parasitic particles. A film thickness of up to 3 μm has been achieved while keeping the root mean square below 0.7 nm. Record carrier mobilities of 155 cm2 V-1 s-1 (2.2 μm) and 163 cm2 V-1 s-1 (3 μm) at room temperature were measured for (100) β-Ga2O3 films with carrier concentrations of 5.7 × 1016 and 7.1 × 1016 cm-3, respectively. Analysis of temperature-dependent Hall mobility and carrier concentration data revealed a low background compensating acceptor concentration of 4 × 1015 cm-3.
- ItemRefractory metal-based ohmic contacts on β-Ga2O3 using TiW(Melville, NY : AIP Publ., 2022) Tetzner, Kornelius; Schewski, Robert; Popp, Andreas; Anooz, Saud Bin; Chou, Ta-Shun; Ostermay, Ina; Kirmse, Holm; Würfl, JoachimThe present work investigates the use of the refractory metal alloy TiW as a possible candidate for the realization of ohmic contacts to the ultrawide bandgap semiconductor β-Ga2O3. Ohmic contact properties were analyzed by transfer length measurements of TiW contacts annealed at temperatures between 400 and 900 °C. Optimum contact properties with a contact resistance down to 1.5 × 10-5 ω cm2 were achieved after annealing at 700 °C in nitrogen on highly doped β-Ga2O3. However, a significant contact resistance increase was observed at annealing temperatures above 700 °C. Cross-sectional analyses of the contacts using scanning transmission electron microscopy revealed the formation of a TiOx interfacial layer of 3-5 nm between TiW and β-Ga2O3. This interlayer features an amorphous structure and most probably possesses a high amount of vacancies and/or Ga impurities supporting charge carrier injection. Upon annealing at temperatures of 900 °C, the interlayer increases in thickness up to 15 nm, featuring crystalline-like properties, suggesting the formation of rutile TiO2. Although severe morphological changes at higher annealing temperatures were also verified by atomic force microscopy, the root cause for the contact resistance increase is attributed to the structural changes in thickness and crystallinity of the interfacial layer.