3 results
Search Results
Now showing 1 - 3 of 3
- ItemRelations between Structure, Activity and Stability in C3N4 Based Photocatalysts Used for Solar Hydrogen Production(Basel : MDPI, 2018-1-29) Sivasankaran, Ramesh P.; Rockstroh, Nils; Hollmann, Dirk; Kreyenschulte, Carsten R.; Agostini, Giovanni; Lund, Henrik; Acharjya, Amitava; Rabeah, Jabor; Bentrup, Ursula; Junge, Henrik; Thomas, Arne; Brückner, AngelikaSolar hydrogen production from water could be a sustainable and environmentally friendly alternative to fossil energy carriers, yet so far photocatalysts active and stable enough for large-scale applications are not available, calling for advanced research efforts. In this work, H2 evolution rates of up to 1968 and 5188 μmol h−1 g−1 were obtained from aqueous solutions of triethanolamine (TEOA) and oxalic acid (OA), respectively, by irradiating composites of AgIn5S8 (AIS), mesoporous C3N4 (CN, surface area >150 m2/g) and ≤2 wt.% in-situ photodeposited Pt nanoparticles (NPs) with UV-vis (≥300 nm) and pure visible light (≥420 nm). Structural properties and electron transport in these materials were analyzed by XRD, STEM-HAADF, XPS, UV-vis-DRS, ATR-IR, photoluminescence and in situ-EPR spectroscopy. Initial H2 formation rates were highest for Pt/CN, yet with TEOA this catalyst deactivated by inclusion of Pt NPs in the matrix of CN (most pronounced at λ ≥ 300 nm) while it remained active with OA, since in this case Pt NPs were enriched on the outermost surface of CN. In Pt/AIS-CN catalysts, Pt NPs were preferentially deposited on the surface of the AIS phase which prevents them from inclusion in the CN phase but reduces simultaneously the initial H2 evolution rate. This suggests that AIS hinders transport of separated electrons from the CN conduction band to Pt NPs but retains the latter accessible by protons to produce H2.
- ItemDevelopment of Active and Stable Low Nickel Content Catalysts for Dry Reforming of Methane(Basel : MDPI, 2017-5-16) Ha, Quan Luu Manh; Armbruster, Udo; Atia, Hanan; Schneider, Matthias; Lund, Henrik; Agostini, Giovanni; Radnik, Jörg; Vuong, Huyen Thanh; Martin, AndreasMethane dry reforming (DRM) was investigated over highly active Ni catalysts with low metal content (2.5 wt %) supported on Mg-Al mixed oxide. The aim was to minimize carbon deposition and metal sites agglomeration on the working catalyst which are known to cause catalyst deactivation. The solids were characterized using N2 adsorption, X-ray diffraction, temperature-programmed reduction, X-ray photoelectron spectroscopy, and UV-Vis diffuse reflectance spectroscopy. The results showed that MgO-Al2O3 solid solution phases are obtained when calcining Mg-Al hydrotalcite precursor in the temperature range of 550–800 °C. Such phases contribute to the high activity of catalysts with low Ni content even at low temperature (500 °C). Modifying the catalyst preparation with citric acid significantly slows the coking rate and reduces the size of large octahedrally coordinated NiO-like domains, which may easily agglomerate on the surface during DRM. The most effective Ni catalyst shows a stable DRM course over 60 h at high weight hourly space velocity with very low coke deposition. This is a promising result for considering such catalyst systems for further development of an industrial DRM technology.
- ItemNb-modified Ce/Ti oxide catalyst for the selective catalytic reduction of NO with NH3 at low temperature(Basel : MDPI, 2018) Mosrati, Jawaher; Atia, Hanan; Eckelt, Reinhard; Lund, Henrik; Agostini, Giovanni; Bentrup, Ursula; Rockstroh, Nils; Keller, Sonja; Armbruster, Udo; Mhamdi, MouradRecently, great attention has been paid to Ceria-based materials for selective catalytic reduction (SCR) with NH3 owing to their unique redox, oxygen storage, and acid-base properties. Two series of bimetallic catalysts issued from Titania modified by Ce and Nb were prepared by the one-step sol-gel method (SG) and by the sol-gel route followed by impregnation (WI). The resulting core-shell and bulk catalysts were tested in NH3-SCR of NOx. The impregnated Nb5/Ce40/Ti100 (WI) catalyst displayed 95% NOx conversion at 200 °C (GHSV = 60,000 mL·g−1·h−1, 1000 ppm NOx, 1000 ppm NH3, 5% O2/He) without forming N2O. The catalysts were characterized by various methods including ICP-OES, N2-physisorption, XRD, Raman, NH3-TPD, DRIFTS, XPS, and H2-TPR. The results showed that the introduction of Nb decreases the surface area and strengthens the surface acidity. This behavior can be explained by the strong interaction between Ceria and Titania which generates Ce-O-Ti units, as well as a high concentration of amorphous or highly dispersed Niobia. This should be the reason for the excellent performance of the catalyst prepared by the sol-gel method followed by impregnation. Furthermore, Nb5/Ce40/Ti100 (WI) has the largest NH3 adsorption capacity, which is helpful to promote the NH3-SCR reaction. The long-term stability and the effect of H2O on the catalysts were also evaluated.