2 results
Search Results
Now showing 1 - 2 of 2
- ItemEffect of minor gallium addition on corrosion, passivity, and antibacterial behaviour of novel β-type Ti–Nb alloys(Sao Paulo : ABM, 2023) Akman, Adnan; Alberta, Ludovico Andrea; Giraldo-Osorno, Paula Milena; Turner, Adam Benedict; Hantusch, Martin; Palmquist, Anders; Trobos, Margarita; Calin, Mariana; Gebert, AnnettMetastable Ti–Nb alloys are promising bone-implant materials due to improved mechanical biofunctionality and biocompatibility. To overcome increasing bacterial infection risk, alloying with antibacterial elements is a promising strategy. This study investigates the effect of minor gallium (Ga) additions (4, 8 wt% Ga) to as-cast and solution-treated β-type Ti–45Nb-based alloy (96(Ti–45Nb)-4Ga, 92(Ti–45Nb)-8Ga (wt.%)) on corrosion and passive film properties, as well as cytocompatibility and antibacterial activity. The electrochemical properties were evaluated by potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), and Mott-Schottky analyses in phosphate-buffered saline (PBS). X-ray photoelectron spectroscopy (XPS) was performed to analyze the chemical composition of passive films. Early adhesion and viability of macrophages and Staphylococcus aureus were assessed by nucleocounting and colony-forming unit counting, respectively. The results showed that high corrosion resistance and passive film properties of Ti–45Nb are retained and even slightly improved with Ga. EIS results revealed that Ga addition improves the passive film resistance. XPS measurements of 92(Ti–45Nb)-8Ga show that the passive film contains Ti-, Nb- and Ga-based oxides, implying the formation of mixed (Ti–Nb-Ga) oxides. In addition, marginal Ga ion release rate was detected under free corrosion conditions. Therefore, it can be assumed that Ga species may contribute to passive film formation on Ga-containing alloys. The 92(Ti–45Nb)-8Ga elicited an antibacterial effect against S. aureus compared to cp-Ti at 4 h. Moreover, Ga-containing alloys showed good cytocompatibility with THP-1 macrophages at 24 h. In conclusion, it was demonstrated that Ga additions to Ti–45Nb are beneficial to corrosion resistance and showed promising initial host and bacterial interactions.
- ItemDesigning Gallium-Containing Hydroxyapatite Coatings on Low Modulus Beta Ti-45Nb Alloy(Basel : MDPI, 2023) Vishnu, Jithin; Voss, Andrea; Hoffmann, Volker; Alberta, Ludovico Andrea; Akman, Adnan; Shankar, Balakrishnan; Gebert, Annett; Calin, MarianaLow-modulus β-type Ti-45Nb alloy is a promising implant material due to its good mechanical biocompatibility, non-toxicity, and outstanding corrosion resistance. Its excellent chemical stability brings new challenges to chemical surface modification treatments, which are indispensable for both osteogenesis and antibacterial performance. Coatings containing metal ions as anti-microbial agents can be an effective way to reduce implant-associated infections caused by bacterial biofilm. Gallium ion (Ga3+) has the potential to reduce bacterial viability and biofilm formation on implant surfaces. In this study, a novel two-step process has been proposed for Ga3+ incorporation in hydroxyapatite (HAP) to develop bioactive and antibacterial surfaces on Ti-45Nb alloy. For the generation of bioactive surface states, HAP electrodeposition was conducted, followed by wet chemical immersion treatments in gallium nitrate (1 mM). Different buffers such as phosphate, sodium bicarbonate, ammonium acetate, and citrate were added to the solution to maintain a pH value in the range of 6.5–6.9. Coating morphology and HAP phases were retained after treatment with gallium nitrate, and Ga3+ ion presence on the surface up to 1 wt.% was confirmed. Combining Ga and HAP shows great promise to enable the local delivery of Ga3+ ions and consequent antibacterial protection during bone regeneration, without using growth factors or antibiotics.