2 results
Search Results
Now showing 1 - 2 of 2
- ItemInsights into surface modification and erosion of multi-element arc cathodes using a novel multilayer cathode design(Melville, NY : American Inst. of Physics, 2020) Golizadeh, Mehran; Anders, André; Martin, Francisca Mendez; Kolozsvári, Szilard; Franz, RobertNowadays, multi-element cathodes are frequently employed to grow multi-element thin films and coatings using cathodic arc deposition processes. During cathode erosion, the cathode spot sequentially ignites on the cathode surface and imposes melting-solidification cycles that lead to material intermixing and the formation of a modified layer on the cathode surface. To allow us to study these surface modifications, a 10 µm thick Mo/Al multilayer coating was sputter-deposited onto a standard Ti arc cathode. This cathode was eroded by a dc steered arc discharge for a short duration enabling the observation of single craters formed by type 1 and 2 cathode spots. Furthermore, separated clusters of overlapping craters and a fully eroded surface caused by different stages of erosion were differentiated when scanning the erosion track in the lateral direction. Cross sections of single craters were prepared by focused ion beam techniques while metallographic methods were applied to obtain cross sections of overlapping craters and the modified layer. The layers of the multilayer coating acted as trace markers providing new insights into the material intermixing within craters, the material displacements during crater formation, the plasma pressure acting on the craters, and the temperature gradient (heat-affected zone) below the craters. The observations are discussed within the framework of established arc crater formation models. © 2020 Author(s).
- ItemInfluence of wavelength and accumulated fluence at picosecond laser-induced surface roughening of copper on secondary electron yield(Melville, NY : American Inst. of Physics, 2023) Bez, Elena; Himmerlich, Marcel; Lorenz, Pierre; Ehrhardt, Martin; Gunn, Aidan Graham; Pfeiffer, Stephan; Rimoldi, Martino; Taborelli, Mauro; Zimmer, Klaus; Chiggiato, Paolo; Anders, AndréUltrashort-pulse laser processing of copper is performed in air to reduce the secondary electron yield (SEY). By UV (355 nm), green (532 nm), and IR (1064 nm) laser-light induced surface modification, this study investigates the influence of the most relevant experimental parameters, such as laser power, scanning speed, and scanning line distance (represented as accumulated fluence) on the ablation depth, surface oxidation, topography, and ultimately on the SEY. Increasing the accumulated laser fluence results in a gradual change from a Cu 2 O to a CuO-dominated surface with deeper micrometer trenches, higher density of redeposited surface particles from the plasma phase, and a reduced SEY. While the surface modifications are less pronounced for IR radiation at low accumulated fluence (,1000 J/cm2 ), analogous results are obtained for all wavelengths when reaching the nonlinear absorption regime, for which the SEY maximum converges to 0.7. Furthermore, independent of the extent of the structural transformations, an electron-induced surface conditioning at 250 eV allows a reduction of the SEY maximum below unity at doses of 5×10 -4 C/mm2 . Consequently, optimization of processing parameters for application in particle accelerators can be obtained for a sufficiently low SEY at controlled ablation depth and surface particle density, which are factors that limit the surface impedance and the applicability of the material processing for ultrahigh vacuum systems. The relations between pro- cessing parameters and surface features will provide guidance in treating the surface of vacuum components, especially beam screens of selected magnets of the Large Hadron Collider or of future colliders.