7 results
Search Results
Now showing 1 - 7 of 7
- ItemTSFZ Growth of Eu-Substituted Large-Size LSCO Crystals(Basel : MDPI, 2022) Voloshyna, Olesia; Romaka, Vitaliy V.; Karmakar, Koushik ;Seiro, Silvia; Maljuk, Andrey; Büchner, BerndThe travelling solvent floating zone (TSFZ) growth of Eu-substituted LSCO (La1.81−xEuxSr0.19CuO4, with nominal x = 0 ÷ 0.4) single crystals was systematically explored for the first time. The substitution of La with Eu considerably decreased the decomposition temperature. Optimal growth parameters were found to be: oxygen pressure 9.0–9.5 bars; Eu-free CuO-poor solvent (66 mol% CuO) with a molar ratio of La2O3:SrCO3:CuO = 4:4.5:16.5 and growth rate 0.6 mm/hour. The obtained single crystals were characterized with optical polarized microscopy, X-ray diffraction and energy-dispersive X-ray spectroscopy analysis. The solubility of Eu in LSCO appeared to be limited to x~0.36–0.38 under the used conditions. The substitution of La3+ with smaller Eu3+ ions led to a structural transition from tetragonal with space group I4/mmm for La1.81Sr0.19CuO4 (x = 0) to orthorhombic with space group Fmmm for La1.81−xSr0.19EuxCuO4 (x = 0.2, 0.3, 0.4), and to a substantial shrinking of the c-axis from 13.2446 Å (x = 0.0) to 13.1257 Å (x = 0.4). Such structural changes were accompanied by a dramatic decrease in the superconducting critical temperature, Tc, from 29.5 K for x = 0 to 13.8 K for 0.2. For x ≥ 0.3, no superconductivity was detected down to 4 K.
- ItemFlux Growth and Characterization of Bulk InVO4 Crystals(Basel : MDPI, 2023) Voloshyna, Olesia; Gorbunov, Mikhail V.; Mikhailova, Daria; Maljuk, Andrey; Seiro, Silvia; Büchner, BerndThe flux growth of InVO4 bulk single crystals has been explored for the first time. The reported eutectic composition at a ratio of V2O5:InVO4 = 1:1 could not be used as a self-flux since no sign of melting was observed up to 1100 °C. Crystals of InVO4 of typical size 0.5 × 1 × 7 mm3 were obtained using copper pyrovanadate (Cu2V2O7) as a flux, using Pt crucibles. X-ray powder diffraction confirmed the orthorhombic Cmcm structure. Rests of the flux material were observed on the sample surface, with occasional traces of Pt indicating some level of reaction with the crucible. X-ray absorption spectroscopy showed that oxidation states of indium and vanadium ions are +3 and +5, respectively. The size and high quality of the obtained InVO4 crystals makes them excellent candidates for further study of their physical properties.
- ItemFloating Zone Growth of Pure and Pb-Doped Bi-2201 Crystals(Basel : MDPI, 2024) Roslova, Maria; Büchner, Bernd; Maljuk, AndreyIn this review, we summarize recent progress in crystal growth and understanding of the influence of crystal structure on superconductivity in pure and Pb-doped Bi2Sr2CuOy (Bi-2201) materials belonging to the overdoped region of high-temperature cuprate superconductors. The crystal growth of Bi-2201 superconductors faces challenges due to intricate materials chemistry and the lack of knowledge of corresponding phase diagrams. Historically, a crucible-free floating zone method emerged as the most promising growth approach for these materials, resulting in high-quality single crystals. This review outlines the described methods in the literature and the authors’ synthesis endeavors encompassing Pb-doped Bi-2201 crystals, provides a detailed structural characterization of as-grown and post-growth annealed samples, and highlights optimal growth conditions that yield large-size, single-phase, and compositionally homogeneous Bi-2201 single crystals.
- ItemLaser-Assisted Floating Zone Growth of BaFe2S3 Large-Sized Ferromagnetic-Impurity-Free Single Crystals(Basel : MDPI, 2021) Amigó, Maria Lourdes; Maljuk, Andrey; Manna, Kaustuv; Stahl, Quirin; Felser, Claudia; Hess, Christian; Wolter, Anja U.B.; Geck, Jochen; Seiro, Silvia; Büchner, BerndThe quasi-one-dimensional antiferromagnetic insulator BaFe2S3 becomes superconducting under a hydrostatic pressure of ∼10 GPa. Single crystals of this compound are usually obtained by melting and further slow cooling of BaS or Ba, Fe, and S, and are small and needle-shaped (few mm long and 50–200 μm wide). A notable sample dependence on the antiferromagnetic transition temperature, transport behavior, and presence of superconductivity has been reported. In this work, we introduce a novel approach for the growth of high-quality single crystals of BaFe2S3 based on a laser-assisted floating zone method that yields large samples free of ferromagnetic impurities. We present the characterization of these crystals and the comparison with samples obtained using the procedure reported in the literature.
- ItemTuning Magnetic and Transport Properties in Quasi-2D (Mn1−xNix)2P2S6 Single Crystals(Basel : MDPI, 2021) Shemerliuk, Yuliia; Zhou, Yonghui; Yang, Zhaorong; Cao, Gang; Wolter, Anja U.; Büchner, Bernd; Aswartham, SaicharanWe report an optimized chemical vapor transport method to grow single crystals of (Mn1−xNix)2P2S6 where x = 0, 0.3, 0.5, 0.7, and 1. Single crystals up to 4 mm × 3 mm × 200 μm were obtained by this method. As-grown crystals are characterized by means of scanning electron microscopy and powder X-ray diffraction measurements. The structural characterization shows that all crystals crystallize in monoclinic symmetry with the space group C2/m (No. 12). We have further investigated the magnetic properties of this series of single crystals. The magnetic measurements of the all as-grown single crystals show long-range antiferromagnetic order along all principal crystallographic axes. Overall, the Néel temperature TN is non-monotonous; with increasing Ni2+ doping, the temperature of the antiferromagnetic phase transition first decreases from 80 K for pristine Mn2P2S6 (x = 0) up to x = 0.5 and then increases again to 155 K for pure Ni2P2S6 (x = 1). The magnetic anisotropy switches from out-of-plane to in-plane as a function of composition in (Mn1−xNix)2P2S6 series. Transport studies under hydrostatic pressure on the parent compound Mn2P2S6 evidence an insulator-metal transition at an applied critical pressure of ~22 GPa.
- ItemSynthesis and Physical Properties of Iridium-Based Sulfide Ca1−xIr4S6(S2) [x = 0.23–0.33](Basel : MDPI, 2022) Vogl, Michael; Valldor, Martin; Piening, Roman Boy; Efremov, Dmitri V.; Büchner, Bernd; Aswartham, SaicharanWe present the synthesis and characterization of the iridium-based sulfide Ca1−xIr4S6(S2). Quality and phase analysis were conducted by means of energy-dispersive X-ray spectroscopy (EDXS) and powder X-ray diffraction (XRD) techniques. Structure analysis reveals a monoclinic symmetry with the space group C 1 2/m 1 (No. 12), with the lattice constants a = 15.030 (3) Å, b = 3.5747 (5) Å and c = 10.4572 (18) Å. Both X-ray diffraction and EDXS suggest an off-stoichiometry of calcium, leading to the empirical composition Ca1−xIr4.0S6(S2) [x = 0.23–0.33]. Transport measurements show metallic behavior of the compound in the whole range of measured temperatures. Magnetic measurements down to 1.8 K show no long range order, and Curie–Weiss analysis yields θCW = −31.4 K, suggesting that the compound undergoes a magnetic state with short range magnetic correlations. We supplement our study with calculations of the band structure in the framework of the density functional theory.
- ItemCurcumin and Graphene Oxide Incorporated into Alginate Hydrogels as Versatile Devices for the Local Treatment of Squamous Cell Carcinoma(Basel : MDPI, 2022) Madeo, Lorenzo Francesco; Sarogni, Patrizia; Cirillo, Giuseppe; Vittorio, Orazio; Voliani, Valerio; Curcio, Manuela; Shai-Hee, Tyler; Büchner, Bernd; Mertig, Michael; Hampel, SilkeWith the aim of preparing hybrid hydrogels suitable for use as patches for the local treatment of squamous cell carcinoma (SCC)-affected areas, curcumin (CUR) was loaded onto graphene oxide (GO) nanosheets, which were then blended into an alginate hydrogel that was crosslinked by means of calcium ions. The homogeneous incorporation of GO within the polymer network, which was confirmed through morphological investigations, improved the stability of the hybrid system compared to blank hydrogels. The weight loss in the 100–170 °C temperature range was reduced from 30% to 20%, and the degradation of alginate chains shifted to higher temperatures. Moreover, GO enhanced the stability in water media by counteracting the de-crosslinking process of the polymer network. Cell viability assays showed that the loading of CUR (2.5% and 5% by weight) was able to reduce the intrinsic toxicity of GO towards healthy cells, while higher amounts were ineffective due to the antioxidant/prooxidant paradox. Interestingly, the CUR-loaded systems were found to possess a strong cytotoxic effect in SCC cancer cells, and the sustained CUR release (~50% after 96 h) allowed long-term anticancer efficiency to be hypothesized.