    Perpendicular magnetic anisotropy in the Heusler alloy Co2TiSi/GaAs(001) hybrid structure
    (New York : American Institute of Physics, 2015) Dau, M.T.; Jenichen, B.; Herfort, J.
    Investigation of the thickness dependence of the magnetic anisotropy in B2-type Co2TiSi films on GaAs(001), shows a pronounced perpendicular magnetic anisotropy at 10 K for thicknesses up to 13.5 nm. We have evidenced that the interfacial anisotropy induced by interface clusters has a strong influence on the perpendicular magnetic anisotropy of this hybrid structure, especially at temperatures lower than the blocking temperature of the clusters (28 K). However, as this influence can be ruled out at higher temperatures, the perpendicular magnetic anisotropy which is found to persist up to room-temperature can be ascribed to the magnetic properties of the Co2TiSi films. For thicknesses larger than 15.0 nm, we observe an alignment of the magnetic easy axis parallel to the sample surface, which is most likely due to the shape anisotropy and the film structure.
  • Thumbnail Image
    Item
    Structural properties of Co2TiSi films on GaAs(001)
    (New York : American Institute of Physics, 2016) Jenichen, B.; Herfort, J.; Hanke, M.; Jahn, U.; Kong, X.; Dau, M.T.; Trampert, A.; Kirmse, H.; Erwin, S.C.
    Co2TiSi films were grown by molecular beam epitaxy on GaAs(001) and analyzed using reflection high-energy electron diffraction, and electron microscopy. In addition, X-ray diffraction was combined with lattice parameter calculations by density functional theory comparing the L21 and B2 structures and considering the influence of non-stoichiometry. Columnar growth is found and attributed to inhomogeneous epitaxial strain from non-random alloying. In films with thicknesses up to 13 nm, these columns may be the origin of perpendicular magnetization with the easy axis perpendicular to the sample surface. We found L21 and B2 ordered regions, however the [Co]/[Ti]-ratio is changing in dependence of the position in the film. The resulting columnar structure is leading to anisotropic B2-ordering with the best order parallel to the axes of the columns.