Effect of Silver Doping on the Superconducting and Structural Properties of YBCO Films Grown by PLD on Different Templates
2022, Shipulin, Ilya A., Thomas, Aleena Anna, Holleis, Sigrid, Eisterer, Michael, Nielsch, Kornelius, Hühne, Ruben
We report the local structural and superconducting properties of undoped and Ag-doped YBa2Cu3O6+x (YBCO) films with a thickness of up to 1 µm prepared by pulsed laser deposition on SrTiO3 (STO) single crystals and on ion-beam-assisted deposition (IBAD) and rolling-assisted biaxially textured substrate (RABiTS)-based metal templates. X-ray diffraction demonstrates the high crystalline quality of the films on both single crystalline substrates and metal-based templates, respectively. Although there was only a slight decrease in Tc of up to 1.5 K for the Ag-doped YBCO films on all substrates, we found significant changes in their transport characteristics. The effect of the silver doping mainly depended on the concentration of silver, the type of substrate, and the temperature and magnetic field. In general, the greatest improvement in Jc over a wide range of magnetic fields and temperatures was observed for the 5%Ag-doped YBCO films on STO substrates, showing a significant increase compared to undoped films. Furthermore, a slight Jc improvement was observed for the 2%Ag-doped YBCO films on the RABiTS templates at temperatures below 65 K, whereas Jc decreased for the Ag-doped films on IBAD-MgO-based templates compared to undoped YBCO films. Using detailed electron microscopy studies, small changes in the local microstructure of the Ag-doped YBCO films were revealed; however, no clear correlation was found with the transport properties of the films.
Structure and superconducting characteristics of magnesium diboride, substitution of boron atoms by oxygen and carbon
2017, Prikhna, Tetiana, Romaka, Vitaliy, Eisterer, Michael, Shapovalov, Andrii, Kozyrev, Artem, Grechnev, Gennadiy, Boutko, Viktor, Goldacker, Wilfried, Habisreuther, Tobias, Vakaliuk, Oleksii, Halbedel, Bernd
An x-ray analysis of MgB2-based materials shows that they contain MgB2 and MgO phases. According to a quantitative Auger analysis (taken after removing the oxidized surface layer by Ar ion etching in the microscope chamber) the MgB2 phase contains some amount of oxygen that approximately corresponds to the composition MgB2.2-1.7O0.4-0.6. Rietveld refinement of the MgB2 phase, based on EDX data with varying B/O content, leads to the composition MgB1.68-1.8O0.2-0.32. Ab-initio modelling of boron substitution by oxygen in MgB2 (ΔH f = -150.6 meV/atom) shows that this is energetically favourable up to the composition MgB1.75O0.25 (ΔH f = -191.4 meV/atom). In contrast to carbon substitution, where very small levels of doping can dramatically affect the superconducting characteristics of the material with concomitant changes in the electron density, oxygen substitution results in very little change in the superconducting properties of MgB2. The formation of vacancies at the Mg site of both MgB2 and substituted MgB1.75O0.25 was modelled as well, but has shown that such processes are energetically disadvantageous (ΔHf of Mg0.875B2 and Mg0.75B1.75O0.25 are equal to -45.5 and -93.5 meV/atom, respectively).