Search Results
Correlation of Electrical Properties and Acoustic Loss in Single Crystalline Lithium Niobate-Tantalate Solid Solutions at Elevated Temperatures
Electrical conductivity and acoustic loss Q−1 of single crystalline Li(Nb,Ta)O3 solid solutions (LNT) are studied as a function of temperature by means of impedance spectroscopy and resonant piezoelectric spectroscopy, respectively. For this purpose, bulk acoustic wave resonators with two different Nb/Ta ratios are investigated. The obtained results are compared to those previously reported for congruent LiNbO3. The temperature dependent electrical conductivity of LNT and LiNbO3 show similar behavior in air at high temperatures from 400 to 700 °C. Therefore, it is concluded that the dominant transport mechanism in LNT is the same as in LN, which is the Li transport via Li vacancies. Further, it is shown that losses in LNT strongly increase above about 500 °C, which is interpreted to originate from conductivity-related relaxation mechanism. Finally, it is shown that LNT bulk acoustic resonators exhibit significantly lower loss, comparing to that of LiNbO3.
Electromechanical losses in carbon- and oxygen-containing bulk AlN single crystals
Bulk single-crystalline aluminum nitride (AlN) is potentially a key component for low-loss high-temperature piezoelectric devices. However, the incorporation of electrically active impurities and defects during growth of AlN may adversely affect the performance of piezoelectric resonators especially at high temperatures. The electrical conductivity and electromechanical losses in bulk AlN single crystals are analyzed in the temperature range of 300–1200 K with respect to various contents of growth-related impurities in them. For AlN with [O]/[C] ≤ 1, an increase of electrical conductivity due to thermal activation of charge carriers in the temperature range of 850–1200 K has been observed and was determined to be a major contribution to electromechanical losses Q−1 rising up to maximum values of about 10−3 at 1200 K. As the oxygen content in AlN increased, the magnitude and the activation energy of high-temperature electrical conductivity increased. In oxygen-dominated AlN, two major thermally activated contributions to electromechanical losses were observed, namely, the anelastic relaxations of point defects at temperatures of 400–800 K and electrical conductivity at T > 800 K.
High-temperature electromechanical loss in piezoelectric langasite and catangasite crystals
Temperature-dependent acoustic loss Q−1 is studied in partially disordered langasite (LGS, La3Ga5SiO14) and ordered catangasite (CTGS, Ca3TaGa3Si2O14) crystals and compared with previously reported CTGS and langatate (LGT, La3Ga5.5Ta0.5O14) data. Two independent techniques, a contactless tone-burst excitation technique and contacting resonant piezoelectric spectroscopy, are used in this study. Contributions to the measured Q−1(T) are determined through fitting to physics-based functions, and the extracted fit parameters, including the activation energies of the processes, are discussed. It is shown that losses in LGS and CTGS are caused by a superposition of several mechanisms, including intrinsic phonon–phonon loss, point-defect relaxations, and conductivity-related relaxations.
Transport and Electromechanical Properties of Ca3TaGa3Si2O14 Piezoelectric Crystals at Extreme Temperatures
Transport mechanisms in structurally ordered piezoelectric Ca3TaGa3Si2O14 (CTGS) single crystals are studied in the temperature range of 1000-1300 °C by application of the isotope 18O as a tracer and subsequent analysis of diffusion profiles of this isotope using secondary ion mass spectrometry (SIMS). Determined oxygen self-diffusion coefficients enable calculation of oxygen ion contribution to the total conductivity, which is shown to be small. Since very low contributions of the cations have to be expected, the total conductivity must be dominated by electron transport. Ion and electron conductivities are governed by different mechanisms with activation energies (1.9±0.1) eV and (1.2±0.07) eV, respectively. Further, the electromechanical losses are studied as a function of temperature by means of impedance spectroscopy on samples with electrodes and a contactless tone-burst excitation technique. At temperatures above 650 °C the conductivity-related losses are dominant. Finally, the operation of CTGS resonators is demonstrated at cryogenic temperatures and materials piezoelectric strain constants are determined from 4.2 K to room temperature. Copyright © Materials Research Society 2019.