3 results
Search Results
Now showing 1 - 3 of 3
- ItemAnalysis of polyethylene-based cold end coatings on glass : Containers with contact angle and IR spectroscopy(Offenbach : Verlag der Deutschen Glastechnischen Gesellschaft, 1999) Geotti-Bianchini, Franco; Preo, MartinaThe aim of cold end coating is to protect the glass surface from abrasive wear with the help of a suitably anchored film of organic material which decreases friction, by preventing direct glass to glass contacts. At present, routine controls on cold end coatings are limited to a lubricity test, i.e. the determination of the slide angle. Α laboratory procedure based on the determination of the contact angle with water is described in this work. It allows one to estimate the coverage with cold end coating locally from the waterrepellence caused by the organic deposit. This method can be used to investigate a ränge of problems associated with glass wettability, including label adhesion, acid etching and washing residues. The contact angle correlates well with the slide angle. Qualitative information on the nature of cold end coatings is obtained by extracting the glass with volatile organic solvents such as methylene chloride, evaporating them and analyzing the residue with infrared spectroscopy. In the case of a coating with RP 40 LT the IR curves show the presence of Polyethylene partially oxidized in order to improve adhesion to the glass surface, besides Polyethylene glycol added as an emulsifying agent. If the cold end coated container is rinsed with water, the glycol dissolves, but the Polyethylene derivative remains strongly anchored. Such bond withstands even drastic washings with water and detergents, alkali or oxidizing acids. Even when the glass is extracted with organic solvents, only a fraction of the deposit is dissolved. Therefore, even a quantitative analysis of the IR spectrum of the extract provides values smaller than the true coverage due to incomplete extraction.
- ItemRecommended procedure for the IR spectroscopic determination of water in soda-lime-silica glass : Report of the International Commission on Glass (ICG) Technical Committee 14 "Gases in Glass"(Offenbach : Verlag der Deutschen Glastechnischen Gesellschaft, 1999) Geotti-Bianchini, Franco; Geißler, Heinz; Krämer, Fritz; Smith, Ian H.The paper illustrates a procedure recommended by Technical Committee 14 (TC14 "Gases in Glass") of the International Commission on Glass (ICG) for the determination of the water content of soda-lime-silica glass by infrared transmittance spectroscopy, based on the two bands at 2.8 and 3.6 μm using as extincdon coefficients 70 and 150 l/(mol · cm), respectively As shown by the result of two intercomparisons, the agreement on the determined water concentration values can be quite satisfactory, within ±20 ppm, provided the procedure to evaluate the spectral curves is closely specified. The selected extinction coefficients are in reasonable agreement with recent evidence obtained using Nuclear Reaction Analysis.
- ItemInfluence of water dissolved in the structure of soda-lime-silica glass on melting, forming and properties: state-of-the-art and controversial issues Report of the International Commission on Glass (ICG) Technical Committee 14 "Gases in Glass"(Offenbach : Verlag der Deutschen Glastechnischen Gesellschaft, 1999) Geotti-Bianchini, Franco; Brown, John T.; Faber, Anne J.; Hessenkemper, Heiko; Kobayashi, Sho; Smith, Ian H.The paper summarizes the information available about the water content of soda-lime-silica glass, the factors that influence it and the influence exerted by water in glass on redox and sulphur retention, on fming, on the melting and forming behaviour, workability and the physical and chemical properties of the melt. Such issues were discussed by the authors in their presentations at the first Forum on Water in Glass, organized in 1997 by Technical Committee 14 (TC 14 "Gases in Glass") of the International Commission on Glass (ICG). The present paper reports the conclusions of the final discussion, highlighting the issues on which consensus was reached (IR spectroscopy is suitable to monitor the water content; the water content of conventionally fired Containers is 300 to 400 ppm and daily oscillations are moderate; water, redox and sulphur interact mutually; water lowers the viscosity; the influence of water content variations on the radiative thermal conductivity is moderate) and the still controversial issues (influence of water and hydroxides in the batch on the final water content; influence of water in the batch and atmosphere on the redox State of the glass; influence of oscillations of OH level on the workability; influence of OH level on ease of forming, product quahty and strength).