Production and characterization of brass-matrix composites reinforced with Ni59Zr20Ti16Si2Sn3 glassy particles
Brass-matrix composites reinforced with 40 and 60 vol.% of Ni59Zr20Ti16Si2Sn3 glassy particles were produced by powder metallurgy. The crystallization behavior and the temperature dependence of the viscosity of the glass reinforcement were studied in detail to select the proper sintering parameters in order to avoid crystallization of the glassy phase during consolidation. The brass-glass powder mixtures were prepared through manual blending as well as by ball milling to analyze the effect of the matrix ligament size on the mechanical properties of the composites. The powder mixtures were then consolidated into highly-dense bulk specimens at temperatures within the supercooled liquid region by hot pressing followed by hot extrusion. The preparation of the powder mixtures has a strong influence on the mechanical behavior of the composites. The strength increases from 500 MPa for pure brass to 740 and 925 MPa for the blended composites with 40 and 60vol.% of glass reinforcement, while the strength increases to 1,240 and 1,640 MPa for the corresponding composites produced by ball milling. Modeling of the mechanical properties indicates that this behavior is related to the reduced matrix ligament size characterizing the milled composites.
Glass-forming ability, phase formation and mechanical properties of glass-forming Cu-Hf-Zr alloys
The influence of Hf additions on the glass-forming ability (GFA), phase formation and mechanical properties of Cu50HfxZr50-x (x = 2,5,10,20 at.%) alloys has been systematically investigated. We report on a distinct correlation between phase formation and GFA of Cu50Zr50-based alloys. Increasing additions of Hf reduce the thermal stability of the high-temperature B2 Cu(Hf,Zr) phase, while the thermal stability of the corresponding undercooled melt is enhanced. The GFA of these alloy series gradually raises up to 10 at.% Hf, whereas at 20 at.%Hf, the GFA is drastically lowered, since the B2 Cu(Hf,Zr) phase becomes unstable and the precipitation of the low-temperature equilibrium phases is favoured. This interrelation determines the microstructure and results in the formation of Cu-Hf-Zr-based bulk metallic glass composites. These composites not only show appreciable macroscopic plastic strain, but also high yield strength.