    Tm3+/Ho3+ co-doped germanate glass double-clad fiber for broadband emission and lasing above 2 µm
    (Washington D.C. : Optical Society of America, 2019) Kochanowicz, Marcin; Zmojda, Jacek; Miluski, Piotr; Baranowska, Agata; Leich, Martin; Schwuchow, Anka; Jäger, Matthias; Kuwik, M.; Pisarska, Johanna; Pisarski, Wojciech A.; Dorosz, Dominik
    In this paper, a 2 µm broadband emission under 796 nm laser diode excitation in low phonon energy GeO2-Ga2O3-BaO glass system is co-doped with 0.7Tm2O3/(0.07-0.7)Ho2O3 (mol%). The widest emission band (where the Tm3+ → Ho3+ energy transfer efficiency is 63%) was obtained for 0.7Tm2O3/0.15Ho2O3 co-doped glass from which a double-clad optical fiber was realized and investigated. Optimization of Tm3+/Ho3+ concentration enabled the acquisition of broadband amplified spontaneous emission (ASE) in double-clad optical fiber with a full width at half maximum (FWHM): 377 nm and 662 nm for 3 dB and 10 dB bandwidth, respectively. ASE spectrum is a result of the superposition of (Tm3+: 3H4 →Η3F4) 1.45 µm, (Tm3+: 3F4 → 3H6) 1.8 µm and (Ho3+:5I7 → 5I8) 2 µm emission bands. Hence, highly rare-earth co-doped germanate glass is characterized by a remarkably broader ASE spectrum than silica and tellurite fibers showed promising lasing properties for their further application in tunable and dual wavelength lasers.In this paper, a 2 µm broadband emission under 796 nm laser diode excitation in low phonon energy GeO2-Ga2O3-BaO glass system is co-doped with 0.7Tm2O3/(0.07-0.7)Ho2O3 (mol%). The widest emission band (where the Tm3+ → Ho3+ energy transfer efficiency is 63%) was obtained for 0.7Tm2O3/0.15Ho2O3 co-doped glass from which a double-clad optical fiber was realized and investigated. Optimization of Tm3+/Ho3+ concentration enabled the acquisition of broadband amplified spontaneous emission (ASE) in double-clad optical fiber with a full width at half maximum (FWHM): 377 nm and 662 nm for 3 dB and 10 dB bandwidth, respectively. ASE spectrum is a result of the superposition of (Tm3+: 3H4 →Η3F4) 1.45 µm, (Tm3+: 3F4 → 3H6) 1.8 µm and (Ho3+:5I7 → 5I8) 2 µm emission bands. Hence, highly rare-earth co-doped germanate glass is characterized by a remarkably broader ASE spectrum than silica and tellurite fibers showed promising lasing properties for their further application in tunable and dual wavelength lasers.
  • Thumbnail Image
    Item
    Yb-doped large mode area fiber for beam quality improvement using local adiabatic tapers with reduced dopant diffusion
    (Washington D.C. : Optical Society of America, 2018) Zhu, Yuan; Leich, Martin; Lorenz, Martin; Eschrich, Tina; Aichele, Claudia; Kobelke, Jens; Bartelt, Hartmut; Jäger, Matthias
    A newly designed all-solid step-index Yb-doped aluminosilicate large mode area fiber for achieving high peak power at near diffraction limited beam quality with local adiabatic tapering is presented. The 45µm diameter fiber core and pump cladding consist of active/passively doped aluminosilicate glass produced by powder sinter technology (REPUSIL). A deliberate combination of innovative cladding and core materials was aspired to achieve low processing temperature reducing dopant diffusion during fiber fabrication, tapering and splicing. By developing a short adiabatic taper, robust seed coupling is achieved by using this Yb-doped LMA fiber as final stage of a nanosecond fiber Master Oscillator Power Amplifier (MOPA) system while maintaining near diffraction limited beam quality by preferential excitation of the fundamental mode. After application of a fiber-based endcap, the peak power could be scaled up to 375 kW with high beam quality and a measured M2 value of 1.3~1.7.A newly designed all-solid step-index Yb-doped aluminosilicate large mode area fiber for achieving high peak power at near diffraction limited beam quality with local adiabatic tapering is presented. The 45µm diameter fiber core and pump cladding consist of active/passively doped aluminosilicate glass produced by powder sinter technology (REPUSIL). A deliberate combination of innovative cladding and core materials was aspired to achieve low processing temperature reducing dopant diffusion during fiber fabrication, tapering and splicing. By developing a short adiabatic taper, robust seed coupling is achieved by using this Yb-doped LMA fiber as final stage of a nanosecond fiber Master Oscillator Power Amplifier (MOPA) system while maintaining near diffraction limited beam quality by preferential excitation of the fundamental mode. After application of a fiber-based endcap, the peak power could be scaled up to 375 kW with high beam quality and a measured M2 value of 1.3~1.7.