3 results
Search Results
Now showing 1 - 3 of 3
- ItemOccurrence of Flux Jumps in MgB2 Bulk Magnets during Pulse-Field Magnetization(Bristol : IOP Publ., 2020) Sakai, N.; Oka, T.; Yamanaka, K.; Dadiel, L.; Oki, H.; Ogawa, J.; Fukui, S.; Scheiter, J.; Häßler, W.; Yokoyama, K; Noudem, J.; Miryala, M.; Murakami, M.The magnetic flux capturing of MgB2 bulk magnets made by spark plasma sintering process has been precisely investigated to clarify the mechanism of flux motions during the pulse-field magnetization processes. The field trapping ratio B T/B P was evaluated as a key parameter of field trapping ability which strongly relates to the heat generation due to the rapid flux motion in the samples. The time dependence of magnetic flux density revealed the actual flux motion which penetrated the samples. The trapped fields B T and field trapping ratios B T/B P of various samples were classified into three regions of 'no flux flow', 'fast flux flow' and 'flux jump' according to the generation of heat and its propagation. A flux jump was observed late at 280 ms from the beginning of PFM process, while the field penetration B P showed its peak at 10 ms. Considering the heat propagation speed, the long-delayed flux jump should be attributed to the macroscopic barriers against the heat propagation to the surface centre of bulk magnet. © Published under licence by IOP Publishing Ltd.
- ItemMagnetic Flux Trapping and Flux Jumps in Pulsed Field Magnetizing Processes in REBCO and Mg-B Bulk Magnets(Bristol : IOP Publ., 2020) Oka, T.; Takeda, A.; Oki, H.; Yamanaka, K.; Dadiel, L.; Yokoyama, K.; Häßler, W.; Scheiter, J.; Sakai, N.; Murakami, M.Pulsed-field magnetization technique (PFM) is expected as a cheap and an easy way for HTS bulk materials for utilizing as intense magnets. As the generation of heat due to magnetic flux motion in bulk magnets causes serious degradation of captured fields, it is important to investigate the flux motions during PFM in various field applications. The authors precisely measured the magnetic flux motion in the cryocooled MgB2 bulk magnets containing various amount of Ti. We classified the motions to "no flux flow (NFF)", "fast flux flow (FFF)", and "flux jump (FJ)" regions. The results showed that addition of Ti shifts the field invasion area to high field areas, and expands the NFF regions. The highest field-trapping appears at the upper end of the NFF region. Since the heat generation and its propagation should attribute to the dissipation of magnetic flux, FFF leads to FJ. Compared with MgB2, we referred to GdBCO as for the flux motion. A flux jump was observed at 30 K when the pulse field of 7 T was applied to the preactivated sample, showing its stability against FJ. © Published under licence by IOP Publishing Ltd.
- ItemShielding Effect on Flux Trapping in Pulsed-Field Magnetizing for Mg-B Bulk Magnet(Bristol : IOP Publ., 2021) Oka, T.; Yamanaka, K.; Sudo, K.; Dadiel, L.; Ogawa, J.; Yokoyama, K.; Häßler, W.; Noudem, J.; Berger, K.; Sakai, N.; Miryala, M.; Murakami, M.MgB2 superconducting bulk materials are characterized as simple and uniform metallic compounds, and capable of trapping field of non-distorted conical shapes. Although pulsed-field magnetization technique (PFM) is expected to be a cheap and an easy way to activate them, the heat generation due to the magnetic flux motion causes serious degradation of captured fields. The authors precisely estimated the flux trapping property of the bulk samples, found that the flux-shielding effect closely attributed to the sample dimensions. The magnetic field capturing of Ti-5.0wt% sample reached the highest value of 0.76 T. The applied field which reached the centre of the sample surface shifted from 1.0 T to 1.2 T with increasing sample thickness from 3.67 mm to 5.80 mm. This means that the shielding effect was enhanced with increasing the sample thickness. Moreover, Ti-addition affected the frequency of flux jump happenings. The occurrence of flux jumps was suppressed in 5.0wt%Ti-added sample. This means that the heat capacity of the compounds was promoted by Ti addition.