4 results
Search Results
Now showing 1 - 4 of 4
- ItemTime‐Dependent Cation Selectivity of Titanium Carbide MXene in Aqueous Solution(Weinheim : Wiley-VCH, 2022) Wang, Lei; Torkamanzadeh, Mohammad; Majed, Ahmad; Zhang, Yuan; Wang, Qingsong; Breitung, Ben; Feng, Guang; Naguib, Michael; Presser, VolkerElectrochemical ion separation is a promising technology to recover valuable ionic species from water. Pseudocapacitive materials, especially 2D materials, are up-and-coming electrodes for electrochemical ion separation. For implementation, it is essential to understand the interplay of the intrinsic preference of a specific ion (by charge/size), kinetic ion preference (by mobility), and crystal structure changes. Ti3C2Tz MXene is chosen here to investigate its selective behavior toward alkali and alkaline earth cations. Utilizing an online inductively coupled plasma system, it is found that Ti3C2Tz shows a time-dependent selectivity feature. In the early stage of charging (up to about 50 min), K+ is preferred, while ultimately Ca2+ and Mg2+ uptake dominate; this unique phenomenon is related to dehydration energy barriers and the ion exchange effect between divalent and monovalent cations. Given the wide variety of MXenes, this work opens the door to a new avenue where selective ion-separation with MXene can be further engineered and optimized.
- ItemOne-step synthesis of nanocrystalline transition metal oxides on thin sheets of disordered graphitic carbon by oxidation of MXenes(Cambridge : Royal Society of Chemistry, 2014) Naguib, Michael; Mashtalir, Olhar; Lukatskaya, Maria R.; Dyatkin, Boris; Zhang, Chuanfang; Presser, Volker; Gogotsi, Yuri; Barsoum, Michael W.Herein we show that heating 2D Ti3C2 in air results in TiO2 nanocrystals enmeshed in thin sheets of disordered graphitic carbon structures that can handle extremely high cycling rates when tested as anodes in lithium ion batteries. Oxidation of 2D Ti3C2 in either CO2 or pressurized water also resulted in TiO2–C hybrid structures. Similarly, other hybrids can be produced, as we show here for Nb2O5/C from 2D Nb2C.
- ItemGrowth of titania and tin oxide from Ti2SnC via rapid thermal oxidation in air for lithium-ion battery application(Oxford [u.a.] : Wiley-Blackwell, 2023) Jolly, Shae; Husmann, Samantha; Presser, Volker; Naguib, MichaelHerein, we report the synthesis of TiO2–SnO2–C/carbide hybrid electrode materials for Li-ion batteries (LIBs) via two different methods of controlled oxidation of layered Ti2SnC. The material was partially oxidized in an open-air furnace (OAF) or using a rapid thermal annealing (RTA) approach to obtain the desired TiO2–SnO2–C/carbide hybrid material; the carbide phase encompassed both residual Ti2SnC and TiC as a reaction product. We tested the oxidized materials as an anode in a half cell to investigate their electrochemical performance in LIBs. Analysis of the various oxidation conditions indicated the highest initial lithiation capacity of 838 mAh/g at 100 mA/g for the sample oxidized in the OAF at 700°C for 1 h. Still, the delithiation capacity dropped to 427 mAh/g and faded over cycling. Long-term cycling demonstrated that the RTA sample treated at 800°C for 30 s was the most efficient, as it demonstrated a reversible capacity of around 270 mAh/g after 150 cycles, as well as a specific capacity of about 150 mAh/g under high cycling rate (2000 mA/g). Given the materials’ promising performance, this processing method could likely be applied to many other members of the MAX family, with a wide range of energy storage applications.
- ItemLayered Nano‐Mosaic of Niobium Disulfide Heterostructures by Direct Sulfidation of Niobium Carbide MXenes for Hydrogen Evolution(Weinheim : Wiley-VCH, 2022) Husmann, Samantha; Torkamanzadeh, Mohammad; Liang, Kun; Majed, Ahmad; Dun, Chaochao; Urban, Jeffrey J.; Naguib, Michael; Presser, VolkerMXene-transition metal dichalcogenide (TMD) heterostructures are synthesized through a one-step heat treatment of Nb2C and Nb4C3. These MXenes are used without delamination or any pre-treatment. Heat treatments accomplish the sacrificial transformation of these MXenes into TMD (NbS2) at 700 and 900 °C under H2S. This work investigates, for the first time, the role of starting MXene phase in the derivative morphology. It is shown that while treatment of Nb2C at 700 °C leads to the formation of pillar-like structures on the parent MXene, Nb4C3 produces nano-mosaic layered NbS2. At 900 °C, both MXene phases, of the same transition metal, fully convert into nano-mosaic layered NbS2 preserving the parent MXene's layered morphology. When tested as electrodes for hydrogen evolution reaction, Nb4C3-derived hybrids show better performance than Nb2C derivatives. The Nb4C3-derived heterostructure exhibits a low overpotential of 198 mV at 10 mA cm−2 and a Tafel slope of 122 mV dec−1, with good cycling stability in an acidic electrolyte.