    Oxygen-deficient oxide growth by subliming the oxide source material: The cause of silicide formation in rare earth oxides on silicon
    (Washington, DC : ACS, 2013) Bierwagen, O.; Proessdorf, A.; Niehle, M.; Grosse, F.; Trampert, A.; Klingsporn, M.
    The fundamental issue of oxygen stoichiometry in oxide thin film growth by subliming the source oxide is investigated by varying the additionally supplied oxygen during molecular beam epitaxy of RE2O3 (RE = Gd, La, Lu) thin films on Si(111). Supplying additional oxygen throughout the entire growth was found to prevent the formation of rare earth silicides observed in films grown without an oxygen source. Postgrowth vacuum annealing of oxygen stoichiometric films did not lead to silicide formation thereby confirming that the silicides do not form as a result of an interface instability at growth temperature in vacuum but rather due to an oxygen deficiency in the source vapor. The average oxygen deficiency of the rare-earth containing species in the source vapor was quantified by the 18O tracer technique and correlated with that of the source material, which gradually decomposed during sublimation. Therefore, any oxide growth by sublimation of the oxide source material requires additional oxygen to realize oxygen stoichiometric films.
  • Thumbnail Image
    Item
    Electron tomography of (In,Ga)N insertions in GaN nanocolumns grown on semi-polar (112̄ 2) GaN templates
    (New York : American Institute of Physics, 2015) Niehle, M.; Trampert, A.; Albert, S.; Bengoechea-Encabo, A.; Calleja, E.
    We present results of scanning transmission electron tomography on GaN/(In,Ga)N/GaN nanocolumns (NCs) that grew uniformly inclined towards the patterned, semi-polar GaN( 11 2 ̄ 2 ) substrate surface by molecular beam epitaxy. For the practical realization of the tomographic experiment, the nanocolumn axis has been aligned parallel to the rotation axis of the electron microscope goniometer. The tomographic reconstruction allows for the determination of the three-dimensional indium distribution inside the nanocolumns. This distribution is strongly interrelated with the nanocolumn morphology and faceting. The (In,Ga)N layer thickness and the indium concentration differ between crystallographically equivalent and non-equivalent facets. The largest thickness and the highest indium concentration are found at the nanocolumn apex parallel to the basal planes.