Melt-mixed thermoplastic composites containing carbon nanotubes for thermoelectric applications
2016, Luo, Jinji, Krause, Beate, Pötschke, Petra
Flexible thermoelectric materials are prepared by melt mixing technique, which can be easily scaled up to industrial level. Hybrid filler systems of carbon nanotubes (CNTs) and copper oxide (CuO), which are environmental friendly materials and contain abundant earth elements, are melt mixed into a thermoplastic matrix, namely polypropylene (PP). With the CNT addition, an electrical network could be built up inside the insulating PP for effective charge transport. The effect of CuO addition is determined by the corresponding CNT concentration. At high CNT concentration, largely above the percolation threshold (φc, ca. 0.1 wt%), the change in the TE properties is small. In contrast, at CNT concentration close to φc, the co-addition of CuO could simultaneously increase the electrical conductivity and Seebeck coefficient. With 5 wt% CuO and 0.8 wt% CNTs where a loose percolated network is formed, the Seebeck coefficient was increased from 34.1 µV/K to 45 µV/K while the electrical conductivity was from 1.6 × 10−3 S/cm to 3.8 × 10−3 S/cm, leading to a power factor of 9.6 × 10−4 µW/mK2 (cf. 1.8 × 10−4 µW/mK2 for the composite with only 0.8 wt% CNTs).
Screening of Different Carbon Nanotubes in Melt-Mixed Polymer Composites with Different Polymer Matrices for Their Thermoelectrical Properties
2019-12-7, Krause, Beate, Barbier, Carine, Levente, Juhasz, Klaus, Maxim, Pötschke, Petra
The aim of this study is to reveal the influences of carbon nanotube (CNT) and polymer type as well as CNT content on electrical conductivity, Seebeck coefficient (S), and the resulting power factor (PF) and figure of merit (ZT). Different commercially available and laboratory made CNTs were used to prepare melt-mixed composites on a small scale. CNTs typically lead to p-type composites with positive S-values. This was found for the two types of multi-walled CNTs (MWCNT) whereby higher Seebeck coefficient in the corresponding buckypapers resulted in higher values also in the composites. Nitrogen doped MWCNTs resulted in negative S-values in the buckypapers as well as in the polymer composites. When using single-walled CNTs (SWCNTs) with a positive S-value in the buckypapers, positive (polypropylene (PP), polycarbonate (PC), poly (vinylidene fluoride) (PVDF), and poly(butylene terephthalate) (PBT)) or negative (polyamide 66 (PA66), polyamide 6 (PA6), partially aromatic polyamide (PARA), acrylonitrile butadiene styrene (ABS)) S-values were obtained depending on the matrix polymer and SWCNT type. The study shows that the direct production of n-type melt-mixed polymer composites from p-type commercial SWCNTs with relatively high Seebeck coefficients is possible. The highest Seebeck coefficients obtained in this study were 66.4 µV/K (PBT/7 wt % SWCNT Tuball) and −57.1 µV/K (ABS/0.5 wt % SWCNT Tuball) for p-and n-type composites, respectively. The highest power factor and ZT of 0.28 µW/m·K2 and 3.1 × 10−4, respectively, were achieved in PBT with 4 wt % SWCNT Tuball.