2019, Chen, Yian, Pötschke, Petra, Pionteck, Jürgen, Voit, Brigitte, Qi, Haisong

Cellulose/graphene oxide (GO)/iron oxide (Fe3O4) composites were prepared by coprecipitating iron salts onto cellulose/GO hydrogels in a basic solution. X-ray photoelectron spectroscopy (XPS), Fourier-transform infrared, and X-ray diffraction characterization showed that Fe3O4 was successfully coated on GO sheets and cellulose. Cellulose/GO/Fe3O4 composites showed excellent catalytic activity by maintaining almost 98% of the removal of acid orange 7 (AO7) and showed stability over 20 consecutive cycles. This performance is attributable to the synergistic effect of Fe3O4 and GO during the heterogeneous Fenton-like reaction. Especially, the cellulose/GO/Fe3O4 composites preserve their activity by keeping the ratio of Fe3+/Fe2+ at 2 even after 20 catalysis cycles, which is supported by XPS analysis.

2017, Krause, Beate, Cohnen, A., Pötschke, Petra, Hickmann, T., Koppler, D., Proksch, B., Kersting, T., Hopmann, C.

In this study, composites based on polypropylene (PP) and different graphite fillers were melt mixed using small scale microcompounder Xplore DSM15 as well as lab-scale co-rotating twin screw extruder Coperion ZSK26Mc. The measurements of the electrical and thermal conductivity as well as mechanical properties of the composites were performed on pressed plates. It was found that the addition of graphite powders having different particle size distributions leads to different increases of the thermal conductivity. For synthetic graphite, the PP composites filled with TIMCAL Timrex® KS500 reached the highest value of thermal conductivity of 0.52 W/(m·K) at 10 vol% loading, whereas this composite was not electrical conductive. Furthermore, the influence of a styrene-ethylene-butylene-styrene block copolymer (SEBS) based impact modifier on the mechanical properties of PP filled with 80 wt% of different synthetic graphites was investigated. For that the proportion of SEBS in the PP component was varied systematically. The conductivities were influenced by the type of graphite and the content of impact modifier. The results indicate that the impact strength of the composite containing TIMCAL Timrex® KS300-1250 can be increased by approx. 100 % when replacing 50 wt% of the PP component by SEBS.

2020, Fritsch, Marco, Coeler, Matthias, Kunz, Karina, Krause, Beate, Marcinkowski, Peter, Pötschke, Petra, Wolter, Mareike, Michaelis, Alexander

A hermetic dense polymer-carbon composite-based current collector foil (PCCF) for lithium-ion battery applications was developed and evaluated in comparison to state-of-the-art aluminum (Al) foil collector. Water-processed LiNi0.5Mn1.5O4 (LMNO) cathode and Li4Ti5O12 (LTO) anode coatings with the integration of a thin carbon primer at the interface to the collector were prepared. Despite the fact that the laboratory manufactured PCCF shows a much higher film thickness of 55 µm compared to Al foil of 19 µm, the electrode resistance was measured to be by a factor of 5 lower compared to the Al collector, which was attributed to the low contact resistance between PCCF, carbon primer and electrode microstructure. The PCCF-C-primer collector shows a sufficient voltage stability up to 5 V vs. Li/Li+ and a negligible Li-intercalation loss into the carbon primer. Electrochemical cell tests demonstrate the applicability of the developed PCCF for LMNO and LTO electrodes, with no disadvantage compared to state-of-the-art Al collector. Due to a 50% lower material density, the lightweight and hermetic dense PCCF polymer collector offers the possibility to significantly decrease the mass loading of the collector in battery cells, which can be of special interest for bipolar battery architectures. © 2020 by the authors. Licensee MDPI, Basel, Switzerland.

2016, Hopmann, C., Windeck, C., Cohnen, A., Onken, J., Krause, Beate, Pötschke, Petra, Hickmann, T.

Bipolar plates constitute the most important structural component in fuel cell stacks. Highly filled thermoplastic composites with high electrical conductivity obtain an increasing importance in the design of bipolar plates as alternative to conventional metallic systems. Thermoplastics (e.g. PP) have suitable properties such as a good processability, chemical resistance, light weight and low production costs. As thermoplastics have low electrical conductivities, conductive fillers have to be included in the matrix. A high content of such fillers (e.g. graphite) in excess of 80 wt.-% is necessary to achieve the desired electrical properties. However, materials with such high filler contents embrittle readily. The workability in injection and compression molding is difficult and the mechanical stability is insufficient in case of strain deformation. As consequence, material failure and an inacceptable amount of damaged goods can be observed during the processing. As no suitable thermoplastic system is available for better mechanical properties, the induction and dispersion of a rubber phase in the thermoplastic matrix can be used to increase the impact strength of the conductive composite. In this research work a ternary composite, based on PP as matrix, EPDM as impact modifier and synthetic graphite as conductive filler, was developed. The material was produced using a 26 mm co-rotating, intermeshing twin-screw extruder. The amounts of PP, EPDM and graphite were varied systematically and a process window was defined that enables improved impact strength and high electrical conductivity of the new material. The results indicate that impact strength can be enhanced by about 99 % with an EPDM content of 30 wt.-% in the PP matrix. The electrical conductivity decreases in a small range with increasing content of EPDM, but the conductivity is still excellent for producing bipolar plates.

2014, Krause, Beate, Pötschke, Petra, Gohs, U.

Polymer modification with high energy electrons (EB) is well established in different applications for many years. It is used for crosslinking, curing, degrading, grafting of polymeric materials and polymerisation of monomers. In contrast to this traditional method, electron induced reactive processing (EIReP) combines the polymer modification with high energy electrons and the melt mixing process. This novel reactive method was used to prepare polymer blends and composites. In this study, both methods were used for the preparation of polyethylene (PE)/ multiwalled carbon nanotubes (MWCNT) composites in the presence of a coupling agent. The influence of MWCNT and type of electron treatment on the gel content, the thermal conductivity, rheological, and electrical properties was investigated whereby as-grown and oxidised MWCNT were used. In the presence of a coupling agent and at an absorbed dose of 40 kGy, the gel content increased from 57 % for the pure PE to 74 % or 88 % by the addition of as-grown (Baytubes® C150P) or oxidised MWCNT, respectively. In comparison to the composites containing the as-grown MWCNTs, the use of the oxidised MWCNTs led to higher melt viscosity and higher storage modulus due to higher yield of filler polymer couplings. The melt viscosity increased due to the addition of MWCNT and crosslinking of PE. The thermal conductivity increased to about 150 % and showed no dependence on the kind of MWCNT and the type of electron treatment. In contrast, the lowest value of electrical volume resistivity was found for the non-irradiated samples and after state of the art electron treatment without any influence of the type of MWCNT. In the case of EIReP, the volume resistivity increased by 2 (as-grown MWCNT) or 3 decades (oxidised MWCNT) depending on the process parameters. © 2014 American Institute of Physics.

2017, Mirkhani, Seyyed Alireza, Arjmand, Mohammad, Sadeghi, Soheil, Krause, Beate, Pötschke, Petra, Sundararaj, Uttandaraman

Employing chemical vapor deposition technique, multi-walled carbon nanotubes (CNTs) were synthesized over Fe catalyst at a broad range of temperatures, i.e. 550° C to 950° C (at 100° C intervals). CNTs were melt-mixed into a polyvinylidene fluoride (PVDF) matrix at various loadings, and then compression molded. Surprisingly, despite the ascending trend of CNT powder conductivity with the synthesis temperature, the nanocomposites made with CNT synthesized at 650° C had significantly lower percolation threshold (around 0.4 wt%) and higher electromagnetic interference shielding effectiveness (EMI SE) (20.3 dB over the X-band for 3.5 wt% CNT and 1.1 mm thickness) than the other temperatures. Exhaustive characterization studies were conducted on both CNTs and composites to unveil their morphological and electrical characteristics. Superior EMI shielding of CNT650° C was attributed to a combination of high carbon purity, aspect ratio, crystallinity, and moderate powder conductivity along with decent state of dispersion within the PVDF matrix.

2019, Müller, Michael Thomas, Krause, Beate, Kretzschmar, Bernd, Pötschke, Petra

In this study commercially available multiwalled carbon nanotubes (2-8 wt.%) were incorporated in polypropylene (PP) by direct powder feeding or by a masterbatch dilution procedure using a twin-screw extruder. The influence of a supplemental, electrical non-conductive talc or electrically conductive carbon black (CB), filler on the resulting composite properties was investigated. In comparison to the direct carbon nanotube (CNT) incorporation the masterbatch dilution step resulted in improved CNT macro dispersion. The use of the supplemental fillers CB or talc does not show a significant influence on the CNT dispersion state. When compared to direct CNT incorporation, the second compounding process involved in masterbatch dilution leads to higher electrical resistivity of injection molded samples. On the other hand, the supplemental fillers talc or CB decreased the electrical resistivity values. With the addition of talc or CB an increase of the Young’s modulus due to the reinforcing effect of the second filler was achieved. However, no synergistic effect between the used supplemental fillers and the CNT on the mechanical properties was obtained.

2017, Socher, Robert, Krause, Beate, Pötschke, Petra

The aim of this study was to decrease the electrical percolation threshold of multiwalled carbon nanotubes (MWCNTs) in a polyamide 12 matrix by the use of additives. Different kinds of additives were selected which either interact with the π-system of the MWCNTs (imidazolium based ionic liquid (IL) and perylene-3,4,9,10-tetracarboxylic dianhydride (PTCDA)) or improve the MWCNT wettability (cyclic butylene terephthalate, CBT). The composites were melt mixed using a DACA microcompounder. The electrical percolation threshold for PA12/MWCNT without additives, measured on compression molded plates, was found between 2.0 and 2.25 wt%. With all used additives, a significant reduction of the electrical percolation threshold could be achieved. Whereas the addition of IL and CBT resulted in MWCNT percolation at around 1.0 wt%, a slightly higher percolation threshold between 1.0 and 1.5 wt% was found for PTCDA as an additive. Interestingly, the electrical resistivity at higher loadings was decreased by nearly two decades when using CBT and one decade after application of PTCDA, whereas IL did not contribute to lower values in this range. In all cases macrodispersion as assessed by light microscopy was not improved and even worse as compared to non-modified composites. In summary, the results illustrate that these kinds of additives are able to improve the performance of PA12 based MWCNT nanocomposites.

2019, Naji, Ahmed, Krause, Beate, Pötschke, Petra, Ameli, Amir

Here, we report multifunctional polycarbonate (PC)-based conductive polymer composites (CPCs) with outstanding performance manufactured by a simple extrusion process and intended for use in bipolar plate (BPP) applications in polymer electrolyte membrane (PEM) fuel cells. CPCs were developed using a ternary conductive filler system containing carbon nanotube (CNT), carbon fiber (CF), and graphite (G) and by introducing di-allyl phthalate (DAP) as a plasticizer to PC matrix. The samples were fabricated using twin-screw extrusion followed by compression molding and the microstructure, electrical conductivity, thermal conductivity, and mechanical properties were investigated. The results showed a good dispersion of the fillers with some degree of interconnection between dissimilar fillers. The addition of DAP enhanced the electrical conductivity and tensile strength of the CPCs. Due to its plasticizing effect, DAP reduced the processing temperature by 75 °C and facilitated the extrusion of CPCs with filler loads as high as 63 wt% (3 wt% CNT, 30 wt% CF, 30 wt% G). Consequently, CPCs with the through-plane electrical, in-plane electrical and thermal conductivities and tensile strength of 4.2 S cm-1, 34.3 S cm-1, 2.9 W m-1 K-1, and 75.4 MPa, respectively, were achieved. This combination of properties indicates the potential of PC-based composites enriched with hybrid fillers and plasticizers as an alternative material for BPP application.

2017, Luo, J., Krause, Beate, Pötschke, Petra

The thermoelectric (TE) performance of electrically conductive thermoplastic composites prepared by melt mixing was investigated. A cost effective widely used in industry polymer, namely polypropylene (PP), was chosen as the matrix to fabricate the composites. Singlewalled carbon nanotubes (SWCNTs), the amount (2 wt%) of which was selected to be above the electrical percolation threshold (< 0.2 wt%), were used to form an electrical conducting network. Besides as-produced SWCNTs plasma modified tubes were employed to study the influence of the functionalization on the morphology, dispersion and TE properties of the PP composites. In addition, melt processing conditions, e.g. temperature, rotation speed, and time during mixing in a small-scale compounder were varied. Furthermore, an ionic liquid (IL, 1-methyl-3-octylimidazolium tetrafluoroborate) was used as a processing additive during melt mixing, which was confirmed to improve the electrical conductivity of the composites. Simultaneous increase in the Seebeck coefficient up to a value of 64 μV/K was recorded, leading to a much better power factor of 0.26 μW/(m·K2) compared to composites without IL. This melt mixing strategy opens new avenues for solvent-free, large scale fabrication of polymer based TE materials.