4 results
Search Results
Now showing 1 - 4 of 4
- ItemMechanical performance and corrosion behaviour of Zr-based bulk metallic glass produced by selective laser melting(Amsterdam : Elsevier B.V., 2020) Deng, L.; Gebert, A.; Zhang, L.; Chen, H.Y.; Gu, D.D.; Kühn, U.; Zimmermann, M.; Kosiba, K.; Pauly, S.Nearly fully dense, glassy Zr52.5Cu17.9Ni14.6Al10Ti5 bulk specimens were fabricated by selective laser melting (SLM) and their behaviour during compressive loading, during wear testing and in a corrosive medium was investigated. Their performance was compared with as-cast material of the same composition. The additively manufactured samples exhibit a yield strength around 1700 MPa combined with a plastic strain of about 0.5% after yielding despite the residual porosity of 1.3%, which is distributed uniformly in the samples. The propagation of shear bands in the bulk metallic glass prepared by SLM was studied. The specific wear rate and the worn surfaces demonstrated that similar wear mechanisms are active in the SLM and the as-cast samples. Hence, manufacturing the glass in layers does not adversely affect the wear properties. The same holds for the corrosion tests, which were carried out in 0.01 M Na2SO4 and 0.1 M NaCl electrolyte. The anodic polarization curves of SLM samples and as-cast samples revealed a similar corrosion behaviour. However, the SLM samples have a slightly reduced susceptibility to pitting corrosion and exhibit an improved surface healing ability, which might be attributed to an improved homogeneity of the additively manufactured glass.
- ItemGuiding shear bands in bulk metallic glasses using stress fields : A perspective from the activation of flow units(Woodbury, NY : Inst., 2020) Kosiba, K.; Scudino, S.; Bednarcik, J.; Bian, J.; Liu, G.; Kühn, U.; Pauly, S.Controlling shear band propagation is the key to obtain ductile metallic glasses. Here, we use a residual stress field to vary the direction of shear band propagation. We ascribe this behavior to the effect of the stress field on the activation of shear transformation zones (STZs) along their characteristic direction and we quantify this contribution to the energy of the process. Because of the progressively adverse orientation of the stress field, the energy stored as shear in the STZ decreases to a level where shear band propagation at alternative angles becomes energetically more favorable. © 2020 authors.
- ItemAmorphous martensite in β-Ti alloys(London : Nature Publishing Group, 2018) Zhang, L.; Zhang, H.; Ren, X.; Eckert, J.; Wang, Y.; Zhu, Z.; Gemming, T.; Pauly, S.Martensitic transformations originate from a rigidity instability, which causes a crystal to change its lattice in a displacive manner. Here, we report that the martensitic transformation on cooling in Ti-Zr-Cu-Fe alloys yields an amorphous phase instead. Metastable β-Ti partially transforms into an intragranular amorphous phase due to local lattice shear and distortion. The lenticular amorphous plates, which very much resemble α′/α″ martensite in conventional Ti alloys, have a well-defined orientation relationship with the surrounding β-Ti crystal. The present solid-state amorphization process is reversible, largely cooling rate independent and constitutes a rare case of congruent inverse melting. The observed combination of elastic softening and local lattice shear, thus, is the unifying mechanism underlying both martensitic transformations and catastrophic (inverse) melting. Not only do we reveal an alternative mechanism for solid-state amorphization but also establish an explicit experimental link between martensitic transformations and catastrophic melting.
- ItemIn-situ tensile testing of ZrCu-based metallic glass composites(London : Nature Publishing Group, 2018) Sun, H.C.; Ning, Z.L.; Wang, G.; Liang, W.Z.; Pauly, S.; Huang, Y.J.; Guo, S.; Xue, X.; Sun, J.F.ZrCu-based bulk metallic glass composites (BMGCs) are well known for their plastic deformability, superior to traditional metallic glasses (MGs), which is attributed to a unique dual-phases structure, namely, the glassy matrix and unstable B2 phase. In the present study, in-situ tensile testing is used to trace the deformation process of a ZrCu-based BMGC. Three deformation stages of the BMGC, i.e., the elastic-elastic stage, the elastic-plastic stage, and the plastic-plastic stage are identified. In the elastic-elastic and elastic-plastic stages, the yield strength and elastic limit are major influenced by the volume fraction of the B2 crystals. In the plastic-plastic stage, the B2 phase stimulates the formation of multiple shear bands and deflects the direction of shear bands by disturbing the stress field in front of the crack tip. The deformation-induced martensitic transformation of the metastable B2 phase contributes to the plasticity and work hardening of the composite. This study highlights the formation and propagation of multiple shear bands and reveals the interactions of shear bands with structural heterogeneities in situ. Especially, the blocking of shear bands by crystals and the martensitic transformation of the B2 phase are critical for the mechanistic deformation process and illustrate the function of the B2 phase in the present BMGCs.