2 results
Search Results
Now showing 1 - 2 of 2
- ItemApproach to Estimate the Phase Formation and the Mechanical Properties of Alloys Processed by Laser Powder Bed Fusion via Casting(Basel : MDPI, 2022) Kühn, Uta; Sander, Jan; Gabrysiak, Katharina Nicole; Giebeler, Lars; Kosiba, Konrad; Pilz, Stefan; Neufeld, Kai; Boehm, Anne Veronika; Hufenbach, Julia KristinA high-performance tool steel with the nominal composition Fe85Cr4Mo8V2C1 (wt%) was processed by three different manufacturing techniques with rising cooling rates: conventional gravity casting, centrifugal casting and an additive manufacturing process, using laser powder bed fusion (LPBF). The resulting material of all processing routes reveals a microstructure, which is composed of martensite, austenite and carbides. However, comparing the size, the morphology and the weight fraction of the present phases, a significant difference of the gravity cast samples is evident, whereas the centrifugal cast material and the LPBF samples show certain commonalities leading finally to similar mechanical properties. This provides the opportunity to roughly estimate the mechanical properties of the material fabricated by LPBF. The major benefit arises from the required small material quantity and the low resources for the preparation of samples by centrifugal casting in comparison to the additive manufacturing process. Concluding, the present findings demonstrate the high attractiveness of centrifugal casting for the effective material screening and hence development of novel alloys adapted to LPBF-processing.
- ItemInvestigating the Static Recrystallization Behavior of 22MnB5 Manganese–Boron Steel through Stress Relaxation Analysis(Basel : MDPI, 2023) Birnbaum, Peter; Pilz, Stefan; Neufeld, Kai; Kunke, AndreasA constitutive model was developed to characterize the static recrystallization (SRX) and evolution of the grain size of the industrially relevant press-hardening steel, 22MnB5, subsequent to the hot forming of sheet metal. Isothermal stress relaxation tests were conducted using the BAEHR 805 A/D thermomechanical simulator, encompassing a temperature range of 950 to 1050 °C, prestrain levels ranging from 0.01 to 0.1, and strain rates spanning from 0.01 to 0.8 s−1. The results obtained from the isothermal stress relaxation tests facilitated the formulation of an Avrami equation-based model, which aptly describes the kinetics of SRX in relation to the temperature, prestrain, and strain rate. Notably, an increase in temperature led to accelerated recrystallization kinetics, signifying temperature-dependent behavior. When the temperature increased from 950 to 1050 °C, the recrystallization time was reduced to approximately one-third. Additionally, the prestrain exhibited a positive influence on the acceleration of SRX kinetics. A quintupling of the prestrain from 0.01 to 0.05 resulted in a reduction of the static recrystallization duration to approximately one-fifth. Among the parameters studied, the strain rate had the least impact on the SRX kinetics, as doubling the strain rate from 0.01 to 0.8 only resulted in a halving of the recrystallization duration. Moreover, an analysis of the microstructural evolution in response to the forming parameters was undertaken. While the grain-size investigation post-isothermal stress relaxation tests provided results in line with the SRX kinetics calculations, the observed effects were comparatively subdued. Furthermore, a comprehensive examination was conducted using electron backscatter diffraction (EBSD) analysis, aiming to explore the effects of specific stress relaxation states on the morphology of martensite. The findings reveal fully recrystallized globulitic microstructures, characterized by relatively minor differences among them.