  • Item
    Phase Transformation Induced by High Pressure Torsion in the High-Entropy Alloy CrMnFeCoNi
    (Basel : MDPI, 2022) Chulist, Robert; Pukenas, Aurimas; Chekhonin, Paul; Hohenwarter, Anton; Pippan, Reinhard; Schell, Norbert; Skrotzki, Werner
    The forward and reverse phase transformation from face-centered cubic (fcc) to hexagonal close-packed (hcp) in the equiatomic high-entropy alloy (HEA) CrMnFeCoNi has been investigated with diffraction of high-energy synchrotron radiation. The forward transformation has been induced by high pressure torsion at room and liquid nitrogen temperature by applying different hydrostatic pressures and large shear strains. The volume fraction of hcp phase has been determined by Rietveld analysis after pressure release and heating-up to room temperature as a function of hydrostatic pressure. It increases with pressure and decreasing temperature. Depending on temperature, a certain pressure is necessary to induce the phase transformation. In addition, the onset pressure depends on hydrostaticity; it is lowered by shear stresses. The reverse transformation evolves over a long period of time at ambient conditions due to the destabilization of the hcp phase. The effect of the phase transformation on the microstructure and texture development and corresponding microhardness of the HEA at room temperature is demonstrated. The phase transformation leads to an inhomogeneous microstructure, weakening of the shear texture, and a surprising hardness anomaly. Reasons for the hardness anomaly are discussed in detail.
  • Item
    High strength nanocrystalline Cu–Co alloys with high tensile ductility
    (Cambridge : Cambridge University Press, 2018) Bachmaier, Andrea; Rathmayr, Georg Benedikt; Schmauch, Jörg; Schell, Norbert; Stark, Andreas; de Jonge, Niels; Pippan, Reinhard
    A supersaturated single-phase Cu–26 at.% Co alloy was produced by high-pressure torsion deformation, leading to a nanocrystalline microstructure with a grain size smaller than 100 nm. The nonequilibrium solid solution decomposed during subsequent isothermal annealing. In situ high-energy X-ray diffraction was used to map changes linked to the separating phases, and the development of a nanoscale Cu–Co composite structure was observed. To gain further information about the relationship of the microstructure and the mechanical properties after phase separation, uniaxial tensile tests were conducted on as-deformed and isothermally annealed samples. Based on the in situ diffraction data, different isothermal annealing temperatures were chosen. Miniaturized tensile specimens with a round cross section were tested, and an image-based data evaluation method enabled the evaluation of true stress–strain curves and strain hardening behavior. The main results are as follows: all microstructural states showed high strength and ductility, which was achieved by a combination of strain-hardening and strain-rate hardening.