2 results
Search Results
Now showing 1 - 2 of 2
- ItemCracking and associated volumetric expansion of NMC811 secondary particles(New York, NY [u.a.] : Elsevier, 2023) Shishvan, S.S.; Fleck, N.A.; McMeeking, R.M.; Deshpande, V.S.Secondary particles comprising a large number of nickel-rich single crystal primary particles are extensively used as storage particles in cathodes of lithium-ion batteries. It is well-established that crack formation in secondary particles is an important degradation mode that contributes to decline in battery performance. Recent X-ray tomographic observations suggest that, at very low C-rates, concentration gradients of lithium within an NMC811 secondary particle are negligible yet cracking still occurs. Additionally, during delithiation the primary particles shrink yet a volumetric expansion of the secondary particle occurs. These observations are explained by a numerical model of distributed cracking due to the extreme anisotropy of lithiation strain of primary particles. The incompatible deformation from grain to grain induces large self-stresses even in the absence of spatial gradients in the lithium concentration. The stress state is sufficient to drive a dynamic catastrophic fracture event, and the associated kinetic energy acquired by the primary particles moves them apart (akin to an explosive event) with the carbon and binder domain surrounding each secondary particle restricting the outward motion of the primary particles. It is predicted that a volume expansion of the secondary particles on the order of 20 % accompanies cracking, in agreement with recently reported observations.
- ItemVacancy diffusion and its consequences for void growth at the interface of a stripping metal electrode and solid electrolyte(New York, NY [u.a.] : Elsevier, 2023) Shishvan, S.S.; Fleck, N.A.; McMeeking, R.M.; Deshpande, V.S.It is commonly observed that voids can nucleate and grow in the lithium anode of a solid state Li-ion battery at a location adjacent to the solid electrolyte during the stripping (discharge) phase of the battery; a similar phenomenon is observed in sodium-based batteries. It is hypothesised in the current literature that the formation of these voids is due to the coalescence of vacancies that have been generated at the electrode/electrolyte interface when metal atoms are oxidized and transported into the electrolyte: the slow diffusion of the vacancies away from the electrolyte interface into the adjacent electrode results in their coalescence and the consequent growth of voids. These hypotheses are challenged in the current study by using the Onsager formalism to generate a variational principle for vacancy diffusion. Our analysis reveals that no driving force exists for the diffusion of vacancies into a homogeneous metal electrode that thins by stripping. This finding is contrary to models in the literature which have mistakenly assumed that the vanishing flux at the current collector prevents rigid body motion (drift) of the electrode which in turn prevents thinning of the electrode during stripping. Based on our analysis, we conclude that vacancy diffusion within a homogeneous electrode is not responsible for the nucleation and growth of voids at the interface between a stripping metal electrode and a solid electrolyte.