    Synthesis of High Crystalline TiO2 Nanoparticles on a Polymer Membrane to Degrade Pollutants from Water
    (Basel : MDPI, 2018-9-5) Fischer, Kristina; Schulz, Paulina; Atanasov, Igor; Abdul Latif, Amira; Thomas, Isabell; Kühnert, Mathias; Prager, Andrea; Griebel, Jan; Schulze, Agnes
    Titanium dioxide (TiO2) is described as an established material to remove pollutants from water. However, TiO2 is still not applied on a large scale due to issues concerning, for example, the form of use or low photocatalytic activity. We present an easily upscalable method to synthesize high active TiO2 nanoparticles on a polyethersulfone microfiltration membrane to remove pollutants in a continuous way. For this purpose, titanium(IV) isopropoxide was mixed with water and hydrochloric acid and treated up to 210 °C. After cooling, the membrane was simply dip-coated into the TiO2 nanoparticle dispersion. Standard characterization was undertaken (i.e., X-ray powder diffraction, scanning electron microscopy, X-ray photoelectron spectroscopy, water permeance, contact angle). Degradation of carbamazepine and methylene blue was executed. By increasing synthesis temperature crystallinity and photocatalytic activity elevates. Both ultrasound modification of nanoparticles and membrane pre-modification with carboxyl groups led to fine distribution of nanoparticles. The ultrasound-treated nanoparticles gave the highest photocatalytic activity in degrading carbamazepine and showed no decrease in degradation after nine times of repetition. The TiO2 nanoparticles were strongly bound to the membrane. Photocatalytic TiO2 nanoparticles with high activity were synthesized. The innovative method enables a fast and easy nanoparticle production, which could enable the use in large-scale water cleaning.
  • Thumbnail Image
    Item
    Criticial Assessment of the Photocatalytic Reduction of Cr(VI) over Au/TiO2
    (Basel : MDPI, 2018-12-3) Ngo, Anh Binh; Nguyen, Hong Lien; Hollmann, Dirk
    The purification of drinking water is one of the most urgent challenges in developing countries, for which the efficient removal of traces of heavy metals, e.g., Cr(IV), represents a key technology. This can be achieved via photocatalysis. In this study, we compare the performance of Au/TiO2 to bare TiO2 P25 catalysts. Furthermore, the influence of the sacrificial reagent citric acid under UV-Vis and Vis excitation was investigated and a detailed investigation of the catalysts before and after reaction was performed. During the photocatalytic reduction of Cr(IV) under acidic conditions, both leaching of Au, as well as absorption of Cr, occur, resulting in new catalyst systems obtained in situ.
  • Thumbnail Image
    Item
    Morphology, Optical Properties and Photocatalytic Activity of Photo- and Plasma-Deposited Au and Au/Ag Core/Shell Nanoparticles on Titania Layers
    (Basel : MDPI, 2018-7-6) Müller, Alexander; Peglow, Sandra; Karnahl, Michael; Kruth, Angela; Junge, Henrik; Brüser, Volker; Scheu, Christina
    Titania is a promising material for numerous photocatalytic reactions such as water splitting and the degradation of organic compounds (e.g., methanol, phenol). Its catalytic performance can be significantly increased by the addition of co-catalysts. In this study, Au and Au/Ag nanoparticles were deposited onto mesoporous titania thin films using photo-deposition (Au) and magnetron-sputtering (Au and Au/Ag). All samples underwent comprehensive structural characterization by grazing incidence X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). Nanoparticle distributions and nanoparticle size distributions were correlated to the deposition methods. Light absorption measurements showed features related to diffuse scattering, the band gap of titania and the local surface plasmon resonance of the noble metal nanoparticles. Further, the photocatalytic activities were measured using methanol as a hole scavenger. All nanoparticle-decorated thin films showed significant performance increases in hydrogen evolution under UV illumination compared to pure titania, with an evolution rate of up to 372 μL H2 h−1 cm−2 representing a promising approximately 12-fold increase compared to pure titania.