    Comparison of the molecular properties and morphology of polypropylenes irradiated under different atmospheres and after annealing
    (Hoboken, NJ [u.a.] : Wiley InterScience, 2006) Krause, Beate; Häußler, Liane; Voigt, Dieter
    Electron-beam irradiation, a well-known way of generating long-chain branching, was used to modify polypropylene. Samples were investigated with differential scanning calorimetry, polarized light microscopy, and size exclusion chromatography. Independently of the atmosphere, postannealing led to the deactivation of residual radicals and to the reduction of the nucleus density. In comparison with the initial polypropylene, the crystallization temperatures increased for nonannealed samples but decreased for annealed samples. Stable products were obtained only by irradiation in nitrogen followed by annealing. A reaction including free radicals with oxygen in the ambient atmosphere led to increasing molar mass degradation and the formation of long-chain branching after Storage. © 2006 Wiley Periodicals, Inc.
  • Thumbnail Image
    Item
    Long-chain branching of polypropylene by electron-beam irradiation in the molten state
    (Hoboken, NJ [u.a.] : Wiley InterScience, 2006) Krause, Beate; Stephan, M.; Volkland, S.; Voigt, D.; Häußler, L.; Dorschner, H.
    The electron-beam irradiation of polymers generates modification effects in the macromolecular structure and material properties. Therefore, irradiation processing is mostly realized in the polymer solid state. In this way, the modification of linear polypropylene may result in long-chain branching of polypropylene macromolecules. The objective of this article is to investigate the effect of a polymer in the molten state during electron-beam irradiation on the macromolecular structure and material properties of polypropylene. For this procedure, a special irradiation vessel (BG3) has been developed in which a rapid transfer of polymer films from the solid state to the molten state and a defined temperature during electron-beam irradiation are realizable. The irradiated samples have been analyzed by high-temperature size exclusion chromatography coupled with a multi-angle laser light scattering detector and differential scanning calorimetry (DSC) measurements. With an increasing irradiation dose, a high reduction of the molar mass and an increasing amount of long-chain branching are found. Compared with irradiation in the solid state, the modification in the molten state leads to a higher degree of branching. The Theological experiments in elongation flow clearly exhibit the existence of long-chain branching. Furthermore, DSC measurements show that the glass-transition temperature and peak temperatures of melting and crystallization decrease. © 2005 Wiley Periodicals, Inc.