Effect of additives on MWCNT dispersion and electrical percolation in polyamide 12 composites
2017, Socher, Robert, Krause, Beate, Pötschke, Petra
The aim of this study was to decrease the electrical percolation threshold of multiwalled carbon nanotubes (MWCNTs) in a polyamide 12 matrix by the use of additives. Different kinds of additives were selected which either interact with the π-system of the MWCNTs (imidazolium based ionic liquid (IL) and perylene-3,4,9,10-tetracarboxylic dianhydride (PTCDA)) or improve the MWCNT wettability (cyclic butylene terephthalate, CBT). The composites were melt mixed using a DACA microcompounder. The electrical percolation threshold for PA12/MWCNT without additives, measured on compression molded plates, was found between 2.0 and 2.25 wt%. With all used additives, a significant reduction of the electrical percolation threshold could be achieved. Whereas the addition of IL and CBT resulted in MWCNT percolation at around 1.0 wt%, a slightly higher percolation threshold between 1.0 and 1.5 wt% was found for PTCDA as an additive. Interestingly, the electrical resistivity at higher loadings was decreased by nearly two decades when using CBT and one decade after application of PTCDA, whereas IL did not contribute to lower values in this range. In all cases macrodispersion as assessed by light microscopy was not improved and even worse as compared to non-modified composites. In summary, the results illustrate that these kinds of additives are able to improve the performance of PA12 based MWCNT nanocomposites.
Thermal conductivity of hybrid filled HDPE nanocomposites
2017, Müller, M. T., Krause, Beate, Kretzschmar, B., Jahn, I., Pötschke, Petra
In this study composite materials based on high-density polyethylene (HDPE) with fillers containing nanostructures were prepared using melt mixing. Vapour Grown Carbon Fibers (VGCF), multiwalled carbon nanotubes (MWCNT) of the types Baytubes® C150P and Nanocyl™ NC7000, anthracite powder, microsilica, organoclay and expanded graphite (EG) as well as mixtures of these fillers were used. The amount and mixing ratios of the hybrid filled systems have been varied to determine their effects on the achievable level of thermal conductivity as measured on compression molded plates. The filler dispersion and phase adhesion were studied using scanning electron microscopy. When limiting the maximum filler content to 10 wt%, the highest enhancement in thermal conductivity by 166% was found for VGCF followed by a 1:1 filler combination of VGCF with EG (148%).
Development of a polymer composite with high electrical conductivity and improved impact strength for the application as bipolar plate
2016, Hopmann, C., Windeck, C., Cohnen, A., Onken, J., Krause, Beate, Pötschke, Petra, Hickmann, T.
Bipolar plates constitute the most important structural component in fuel cell stacks. Highly filled thermoplastic composites with high electrical conductivity obtain an increasing importance in the design of bipolar plates as alternative to conventional metallic systems. Thermoplastics (e.g. PP) have suitable properties such as a good processability, chemical resistance, light weight and low production costs. As thermoplastics have low electrical conductivities, conductive fillers have to be included in the matrix. A high content of such fillers (e.g. graphite) in excess of 80 wt.-% is necessary to achieve the desired electrical properties. However, materials with such high filler contents embrittle readily. The workability in injection and compression molding is difficult and the mechanical stability is insufficient in case of strain deformation. As consequence, material failure and an inacceptable amount of damaged goods can be observed during the processing. As no suitable thermoplastic system is available for better mechanical properties, the induction and dispersion of a rubber phase in the thermoplastic matrix can be used to increase the impact strength of the conductive composite. In this research work a ternary composite, based on PP as matrix, EPDM as impact modifier and synthetic graphite as conductive filler, was developed. The material was produced using a 26 mm co-rotating, intermeshing twin-screw extruder. The amounts of PP, EPDM and graphite were varied systematically and a process window was defined that enables improved impact strength and high electrical conductivity of the new material. The results indicate that impact strength can be enhanced by about 99 % with an EPDM content of 30 wt.-% in the PP matrix. The electrical conductivity decreases in a small range with increasing content of EPDM, but the conductivity is still excellent for producing bipolar plates.
Influence of mixing conditions on carbon nanotube shortening and curling in polycarbonate composites
2017, Krause, Beate, Carval, J., Pötschke, Petra
Polycarbonate composites containing multiwalled carbon nanotubes (MWCNTs, 0.2-2.0 wt%) were melt mixed in small scale at different conditions of screw speed and mixing time to vary the specific mechanical energy (SME) input between 0.4 and 4.0 kWh/kg. Next to the electrical properties of compression molded plates and the MWCNT macrodispersion also the nanotube length and shape were analyzed. For this, the matrix of the composites with 0.75 wt% MWCNT loading was dissolved and the remaining nanotubes were investigated using TEM. It was found that with increasing SME input the number of remaining CNT agglomerates decreases. The MWCNT length decreased from initially about 1.4 micrometers towards 350 nanometers at a SME of 4 kWh/kg and the mean curling values were also reduced. The electrical percolation threshold increases with SME from about 0.4 wt% to 0.6 wt%.