2 results
Search Results
Now showing 1 - 2 of 2
- ItemCellulose-carbon nanotube composite aerogels as novel thermoelectric materials(Amsterdam [u.a.] : Elsevier, 2018) Gnanaseelan, Minoj; Chen, Yian; Luo, Jinji; Krause, Beate; Pionteck, Jürgen; Pötschke, Petra; Qu, HaisongThermoelectric materials based on cellulose/carbon nanotube (CNT) nanocomposites have been developed by a facile approach and the effects of amount (2–10 wt%) and types of CNTs (single-walled carbon nanotubes (SWCNTs) and multi-walled carbon nanotubes (MWCNTs)) on the morphology (films and aerogels) and the thermoelectric properties of the nanocomposites have been investigated. Composite films based on SWCNTs showed significantly higher electrical conductivity (5 S/cm at 10 wt%) and Seebeck coefficient (47.2 μV/K at 10 wt%) compared to those based on MWCNTs (0.9 S/cm and 11 μV/K, respectively). Lyophilization, leading to development of aerogels with sub-micron sized pores, decreased the electrical conductivity for both types by one order of magnitude, but did not affect the Seebeck coefficient of MWCNT based nanocomposites. For SWCNT containing aerogels, higher Seebeck coefficients than for films were measured at 3 and 4 wt% but significantly lower values at higher loadings. CNT addition increased the thermal conductivity from 0.06 to 0.12 W/(m∙K) in the films, whereas the lyophilization significantly reduced it towards values between 0.01 and 0.09 W/(m∙K) for the aerogels. The maximum Seebeck coefficient, power factor, and ZT observed in this study are 49 μV/K for aerogels with 3 wt% SWCNTs, 1.1 μW/(m∙K2) for composite films with 10 wt% SWCNTs, and 7.4 × 10−4 for films with 8 wt% SWCNTs, respectively.
- ItemDevelopment of electrically conductive microstructures based on polymer/CNT nanocomposites via two-photon polymerization(Amsterdam [u.a.] : Elsevier, 2017) Staudinger, U.; Zyla, G.; Krause, Beate; Janke, A.; Fischer, D.; Esen, C.; Voit, B.; Ostendorf, A.Femtosecond laser-induced two-photon polymerization (2PP) of carbon nanofiller doped polymers was utilized to produce electrically conductive microstructures, which are expected to be applicable as microelectronic components or micro-electromechanical systems in sensors. The nanocomposites were processed by compounding an inorganic-organic hybrid material with two different types (short and long) of single walled carbon nanotubes (SWCNTs). Different SWCNT contents were dispersed in the polymer by sonication to adjust the electrical conductivity of the nanocomposites. Low surface resistivity values of ~ 4.6 × 105 Ω/sq. could be measured for coated reference films with a thickness of 30 μm having an exceptionally low SWCNT content of 0.01 wt% of the long type of SWCNTs. In contrast, a higher minimum resistivity of 1.5 × 106 Ω/sq. was exhibited for composites with a higher content, 2 wt%, of short SWCNTs. The structural quality of the microstructures processed by 2PP was mainly influenced by the dispersion quality of the SWCNTs. To characterize the electrical conductivity, conductive atomic force microscopy was applied for the first time. In microstructures with 0.05 wt% of the long type of SWCNTs, a contact current could be detected over a wide range of the measured area visualizing the electrical conductive CNT network, which has not been reported before.