    Textured Sb2Te3 films and GeTe/Sb2Te3 superlattices grown on amorphous substrates by molecular beam epitaxy
    (New York : American Institute of Physics, 2017) Boschker, Jos E.; Tisbi, E.; Placidi, E.; Momand, Jamo; Redaelli, Andrea; Kooi, Bart J.; Arciprete, Fabrizio; Calarco, Raffaella
    The realization of textured films of 2-dimensionally (2D) bonded materials on amorphous substrates is important for the integration of this material class with silicon based technology. Here, we demonstrate the successful growth by molecular beam epitaxy of textured Sb2Te3 films and GeTe/Sb2Te3 superlattices on two types of amorphous substrates: carbon and SiO2. X-ray diffraction measurements reveal that the out-of-plane alignment of grains in the layers has a mosaic spread with a full width half maximum of 2.8°. We show that a good texture on SiO2 is only obtained for an appropriate surface preparation, which can be performed by ex situ exposure to Ar+ ions or by in situ exposure to an electron beam. X-ray photoelectron spectroscopy reveals that this surface preparation procedure results in reduced oxygen content. Finally, it is observed that film delamination can occur when a capping layer is deposited on top of a superlattice with a good texture. This is attributed to the stress in the capping layer and can be prevented by using optimized deposition conditions of the capping layer. The obtained results are also relevant to the growth of other 2D materials on amorphous substrates.
  • Thumbnail Image
    Item
    Structural properties of Co2TiSi films on GaAs(001)
    (New York : American Institute of Physics, 2016) Jenichen, B.; Herfort, J.; Hanke, M.; Jahn, U.; Kong, X.; Dau, M.T.; Trampert, A.; Kirmse, H.; Erwin, S.C.
    Co2TiSi films were grown by molecular beam epitaxy on GaAs(001) and analyzed using reflection high-energy electron diffraction, and electron microscopy. In addition, X-ray diffraction was combined with lattice parameter calculations by density functional theory comparing the L21 and B2 structures and considering the influence of non-stoichiometry. Columnar growth is found and attributed to inhomogeneous epitaxial strain from non-random alloying. In films with thicknesses up to 13 nm, these columns may be the origin of perpendicular magnetization with the easy axis perpendicular to the sample surface. We found L21 and B2 ordered regions, however the [Co]/[Ti]-ratio is changing in dependence of the position in the film. The resulting columnar structure is leading to anisotropic B2-ordering with the best order parallel to the axes of the columns.