Now showing 1 - 2 of 2
  • Thumbnail Image
    Item
    Ba termination of Ge(001) studied with STM
    (Bristol : IOP Publishing, 2015) Koczorowski, W.; Grzela, T.; Radny, M.W.; Schofield, S.R.; Capellini, G.; Czajka, R.; Schroeder, T.; Curson, N.J.
    We use controlled annealing to tune the interfacial properties of a sub-monolayer and monolayer coverages of Ba atoms deposited on Ge(001), enabling the generation of either of two fundamentally distinct interfacial phases, as revealed by scanning tunneling microscopy. Firstly we identify the two key structural phases associated with this adsorption system, namely on-top adsorption and surface alloy formation, by performing a deposition and annealing experiment at a coverage low enough (~0.15 ML) that isolated Ba-related features can be individually resolved. Subsequently we investigate the monolayer coverage case, of interest for passivation schemes of future Ge based devices, for which we find that the thermal evaporation of Ba onto a Ge(001) surface at room temperature results in on-top adsorption. This separation (lack of intermixing) between Ba and Ge layers is retained through successive annealing steps to temperatures of 470, 570, 670 and 770 K although a gradual ordering of the Ba layer is observed at 570 K and above, accompanied by a decrease in Ba layer density. Annealing above 770 K produces the 2D surface alloy phase accompanied by strain relief through monolayer height trench formation. An annealing temperature of 1070 K sees a further change in surface morphology but retention of the 2D surface alloy characteristic. These results are discussed in view of their possible implications for future semiconductor integrated circuit technology.
  • Thumbnail Image
    Item
    Deformation at ambient and high temperature of in situ Laves phases-ferrite composites
    (Bristol : IOP Publishing, 2014) Donnadieu, Patricia; Pohlmann, Carsten; Scudino, Sergio; Blandin, Jean-Jacques; Surreddi, Kumar Babu; Eckert, Jürgen
    The mechanical behavior of a Fe80Zr10Cr10 alloy has been studied at ambient and high temperature. This Fe80Zr10Cr10 alloy, whoose microstructure is formed by alternate lamellae of Laves phase and ferrite, constitutes a very simple example of an in situ CMA phase composite. The role of the Laves phase type was investigated in a previous study while the present work focuses on the influence of the microstructure length scale owing to a series of alloys cast at different cooling rates that display microstructures with Laves phase lamellae width ranging from ∼50 nm to ∼150 nm. Room temperature compression tests have revealed a very high strength (up to 2 GPa) combined with a very high ductility (up to 35%). Both strength and ductility increase with reduction of the lamella width. High temperature compression tests have shown that a high strength (900 MPa) is maintained up to 873 K. Microstructural study of the deformed samples suggests that the confinement of dislocations in the ferrite lamellae is responsible for strengthening at both ambient and high temperature. The microstructure scale in addition to CMA phase structural features stands then as a key parameter for optimization of mechanical properties of CMA in situ composites.