2013, Jenichen, B., Hentschel, T., Herfort, J., Kong, X., Trampert, A., Zizak, I.

Co2FeSi/GaAs(110) and Co2FeSi/GaAs(-1-1-1)B hybrid structures were grown by molecular-beam epitaxy (MBE) and characterized by transmission electron microscopy (TEM) and X-ray diffraction (XRD). The films contain inhomogeneous distributions of ordered L21 and B2 phases. The average stoichiometry could be determined by XRD for calibration of the MBE sources. Diffusion processes lead to inhomogeneities, influencing long-range order. An average L21 ordering of up to 65% was measured by grazing-incidence XRD. Lateral inhomogeneities of the spatial distribution of long-range order in Co2FeSi were imaged using dark-field TEM with superlattice reflections and shown to correspond to variations of the Co/Fe ratio.

2013, Bowlan, P., Kuehn, W., Reimann, K., Woerner, M., Elsaesser, T., Hey, R., Flytzanis, C.

With strong THz pulses, we measure ultrafast transport of electrons, holes, and an electron-hole plasma in GaAs. The transition from ballistic to drift-like transport is strongly influenced by electron-hole scattering.

2018, Lazić, S., Chernysheva, E., Hernández-Mínguez, A., Santos, P.V., van der Meulen, H.P.

On-chip quantum information processing requires controllable quantum light sources that can be operated on-demand at high-speeds and with the possibility of in-situ control of the photon emission wavelength and its optical polarization properties. Here, we report on the dynamic control of the optical emission from core-shell GaN/InGaN nanowire (NW) heterostructures using radio frequency surface acoustic waves (SAWs). The SAWs are excited on the surface of a piezoelectric lithium niobate crystal equipped with a SAW delay line onto which the NWs were mechanically transferred. Luminescent quantum dot (QD)-like exciton localization centers induced by compositional fluctuations within the InGaN nanoshell were identified using stroboscopic micro-photoluminescence (micro-PL) spectroscopy. They exhibit narrow and almost fully linearly polarized emission lines in the micro-PL spectra and a pronounced anti-bunching signature of single photon emission in the photon correlation experiments. When the nanowire is perturbed by the propagating SAW, the embedded QD is periodically strained and its excitonic transitions are modulated by the acousto-mechanical coupling, giving rise to a spectral fine-tuning within a ~1.5 meV bandwidth at the acoustic frequency of ~330 MHz. This outcome can be further combined with spectral detection filtering for temporal control of the emitted photons. The effect of the SAW piezoelectric field on the QD charge population and on the optical polarization degree is also observed. The advantage of the acousto-optoelectric over other control schemes is that it allows in-situ manipulation of the optical emission properties over a wide frequency range (up to GHz frequencies).

2013, Lari, L., Ross, I.M., Walther, T., Black, K., Cheze, C., Geelhaar, L., Riechert, H., Chalker, P.R.

A combination of molecular beam epitaxy (MBE) and atomic layer deposition (ALD) was adopted to fabricate GaN-based core/shell NW structures. ALD was used to deposit a HfO2 shell of onto the MBE grown GaN NWs. Electron transparent samples were prepared by focussed ion beam methods and characterized using state-of-the-art analytical transmission and scanning transmission electron microscopy. The polycrystalline coating was found to be uniform along the whole length of the NWs. Photoluminescence and Raman spectroscopy analysis confirms that the HfO2 ALD coating does not add any structural defect when deposited on the NWs.