    Superconductivity in multi-phase Mg-B-O compounds
    (Amsterdam [u.a.] : Elsevier, 2012) Prikhna, T.; Gawalek, W.; Eisterer, M.; Weber, H.W.; Noudem, J.; Sokolovsky, V.; Chaud, X.; Moshchil, V.; Karpets, M.; Kovylaev, V.; Borimskiy, A.; Tkach, V.; Kozyrev, A.; Kuznietsov, R.; Dellith, J.; Shmidt, C.; Basyuk, T.; Litzkendorf, D.; Karau, F.; Dittrich, U.; Tomsic, M.
    Structures of MgB2-based materials manufactured under pressure (up to 2 GPa) by different methods having high superconducting performance and connectivity are multiphase and contain different Mg-B-O compounds. Some oxygen can be incorporated into MgB2 and boron into MgO structures, MgBx (X=4-20) inclusions contain practically no oxygen. Regulating manufacturing temperature, pressure, introducing additions one can influence oxygen and boron distribution in the materials and thus, affect the formation, amount and sizes of Mg-B-O and MgBx inclusions and changing type of pinning, pinning force and so affect critical current density jc. The boron concentration increase in initial Mg and B mixture allows obtaining sample containing 88.5 wt% of MgB12 with Tc of 37.4 K (estimated magnetically).
  • Thumbnail Image
    Item
    Process flow to integrate nanostructures on silicon grass in surface micromachined systems
    (Bristol : IOP Publ., 2016) Mehner, H.; Müller, L.; Biermann, S.; Hänschke, F.; Hoffmann, M.
    The process flow to integrate metallic nanostructures in surface micromachining processes is presented. The nanostructures are generated by evaporation of microstructured silicon grass with metal. The process flow is based on the lift-off of a thin amorphous silicon layer deposited using a CVD process. All steps feature a low temperature load beneath 120 °C and high compatibility with many materials as only well-established chemicals are used. As a result metallic nanostructures usable for optical applications can be generated as part of multilayered microsystems fabricated in surface micromachining.