4 results
Search Results
Now showing 1 - 4 of 4
- ItemComparison of the molecular properties and morphology of polypropylenes irradiated under different atmospheres and after annealing(Hoboken, NJ [u.a.] : Wiley InterScience, 2006) Krause, Beate; Häußler, Liane; Voigt, DieterElectron-beam irradiation, a well-known way of generating long-chain branching, was used to modify polypropylene. Samples were investigated with differential scanning calorimetry, polarized light microscopy, and size exclusion chromatography. Independently of the atmosphere, postannealing led to the deactivation of residual radicals and to the reduction of the nucleus density. In comparison with the initial polypropylene, the crystallization temperatures increased for nonannealed samples but decreased for annealed samples. Stable products were obtained only by irradiation in nitrogen followed by annealing. A reaction including free radicals with oxygen in the ambient atmosphere led to increasing molar mass degradation and the formation of long-chain branching after Storage. © 2006 Wiley Periodicals, Inc.
- ItemCharacterization of electron beam irradiated polypropylene: Influence of irradiation temperature on molecular and rheological properties(Hoboken, NJ [u.a.] : Wiley InterScience, 2006) Krause, Beate; Voigt, Dieter; Häuβler, Liane; Auhl, Dietmar; Münstedt, HelmutThe aim of the investigations was to analyze the influence of the temperature during the irradiation process of polypropylene on the molar mass, the formation of long chain branching and the final branching topology. A linear isotactic polypropylene homopolymer was modified by electron beam irradiation at different temperatures, with two irradiation doses to insert long chain branching. The Samples were analyzed by size exclusion chromatography coupled with a multiangle laser light scattering detector, by differential scanning calorimetry, and by shear and elongational rheology. The shear and elongational flow behavior isdiscussed in terms of the influence of molecular parameters and used to analyze the topology of the irradiated samples. With increasing temperature, a slight reduction of the molar mass, an increase of long chain branching and an increase of crystallization temperature were found. © 2006 Wiley Periodicals, Inc.
- ItemLong-chain branching of polypropylene by electron-beam irradiation in the molten state(Hoboken, NJ [u.a.] : Wiley InterScience, 2006) Krause, Beate; Stephan, M.; Volkland, S.; Voigt, D.; Häußler, L.; Dorschner, H.The electron-beam irradiation of polymers generates modification effects in the macromolecular structure and material properties. Therefore, irradiation processing is mostly realized in the polymer solid state. In this way, the modification of linear polypropylene may result in long-chain branching of polypropylene macromolecules. The objective of this article is to investigate the effect of a polymer in the molten state during electron-beam irradiation on the macromolecular structure and material properties of polypropylene. For this procedure, a special irradiation vessel (BG3) has been developed in which a rapid transfer of polymer films from the solid state to the molten state and a defined temperature during electron-beam irradiation are realizable. The irradiated samples have been analyzed by high-temperature size exclusion chromatography coupled with a multi-angle laser light scattering detector and differential scanning calorimetry (DSC) measurements. With an increasing irradiation dose, a high reduction of the molar mass and an increasing amount of long-chain branching are found. Compared with irradiation in the solid state, the modification in the molten state leads to a higher degree of branching. The Theological experiments in elongation flow clearly exhibit the existence of long-chain branching. Furthermore, DSC measurements show that the glass-transition temperature and peak temperatures of melting and crystallization decrease. © 2005 Wiley Periodicals, Inc.
- ItemSurface modification of MWCNT and its influence on properties of paraffin/MWCNT nanocomposites as phase change material(Hoboken, NJ [u.a.] : Wiley InterScience, 2020) Avid, Arezoo; Jafari, Seyed Hassan; Khonakdar, Hossein Ali; Ghaffari, Mehdi; Krause, Beate; Pötschke, PetraMultiwalled carbon nanotubes (MWCNTs) were modified by an organo-silane in order to improve their dispersion state and stability in paraffin wax. A family of paraffin-based phase change material (PCM) composites filled with MWCNTs was prepared with different loadings (0, 0.1, 0.5, and 1 wt%) of pristine MWCNTs and organo-silane modified MWCNTs (Si-MWCNT). Structural analyses were performed by means of Fourier transform infrared (FTIR), scanning electron microscopy (SEM), and rheological studies using temperature sweeps. Moreover, phase change transition temperatures and heat of fusion as well as thermal and electrical conductivities of the developed PCM nanocomposites were determined. The SEM micrographs and FTIR absorption bands appearing at approximately 1038 and 1112 cm−1 confirmed the silane modification. Differential scanning calorimetery (DSC) results indicate that the presence of Si-MWCNTs leads to slightly favorable enhancement in the energy storage capacity at the maximum loading. It was also shown that the thermal conductivity of the PCM nanocomposites, in both solid and liquid phases, increased with increasing the MWCNT content independent of the kind of MWCNTs by up to about 30% at the maximum loading of MWCNTs. In addition, the modification of MWCNTs made the samples completely electrically nonconductive, and the electrical surface resistivity of the PCMs containing pristine MWCNTs decreased with increasing MWCNTs loading. Furthermore, the rheological assessment under consecutive cyclic phase change demonstrated that the samples containing modified MWCNTs are more stable compared to the PCM containing pristine MWCNTs. © 2019 Wiley