6 results
Search Results
Now showing 1 - 6 of 6
- ItemMelt mixed composites of polypropylene with singlewalled carbon nanotubes for thermoelectric applications: Switching from p- to n-type behavior by additive addition(Melville, NY : AIP, 2019) Pötschke; Petra; Krause, Beate; Luo, JinjiComposites were prepared with polypropylene (PP) as the matrix and singlewalled CNTs (SWCNTs) of the type TUBALL from OCSiAl Ltd. as the conducting component by melt processing in a small-scale twin-screw compounder. In order to switch the typical p-type behavior of such composites from positive Seebeck coefficients (S) into n-type behavior with negative Seebeck coefficients, a non-ionic surfactant polyoxyethylene 20 cetyl ether (Brij58) was used and compared with a PEG additive, which was shown previously to be able to induce such switching. For PP-2 wt% SWCNT composites Brij58 is shown to result in n-type composites. The negative S values (up to −48.2 µV/K) are not as high as in the case of previous results using PEG (−56.6 µV/K). However, due to the more pronounced effect of Brij58 on the electrical conductivity, the achieved power factors are higher and reach a maximum of 0.144 µW/(m·K2) compared to previous 0.078 µW/(m·K2) with PEG. Dispersion improvement depends on the type of SWCNTs obtained by using varied synthesis/treatment conditions. Solution prepared composites of PEG with SWCNTs also have negative S values, indicating the donation of electrons from PEG to the SWCNTs. However, such composites are brittle and not suitable as thermoelectric materials.
- ItemImpact of synthesis temperature on morphology, rheology and electromagnetic interference shielding of CVD-grown carbon nanotube/polyvinylidene fluoride nanocomposites(Lausanne : Elsevier Sequoia, 2017) Mirkhani, Seyyed Alireza; Arjmand, Mohammad; Sadeghi, Soheil; Krause, Beate; Pötschke, Petra; Sundararaj, UttandaramanEmploying chemical vapor deposition technique, multi-walled carbon nanotubes (CNTs) were synthesized over Fe catalyst at a broad range of temperatures, i.e. 550° C to 950° C (at 100° C intervals). CNTs were melt-mixed into a polyvinylidene fluoride (PVDF) matrix at various loadings, and then compression molded. Surprisingly, despite the ascending trend of CNT powder conductivity with the synthesis temperature, the nanocomposites made with CNT synthesized at 650° C had significantly lower percolation threshold (around 0.4 wt%) and higher electromagnetic interference shielding effectiveness (EMI SE) (20.3 dB over the X-band for 3.5 wt% CNT and 1.1 mm thickness) than the other temperatures. Exhaustive characterization studies were conducted on both CNTs and composites to unveil their morphological and electrical characteristics. Superior EMI shielding of CNT650° C was attributed to a combination of high carbon purity, aspect ratio, crystallinity, and moderate powder conductivity along with decent state of dispersion within the PVDF matrix.
- ItemElectrical and thermal conductivity of polypropylene filled with combinations of carbon fillers(Melville, NY : AIP, 2016) Krause, Beate; Pötschke, PetraThe thermal and electrical conductivity of polymer composites filled with a low content up to 7.5 vol% of different carbon fillers (carbon nanotubes, carbon fibers, graphite nanoplates) were investigated. It was found that the combination of two or three carbon fillers leads to an increase of thermal conductivity up to 193% which is higher than the sum of the effects of both fillers.
- ItemElectrically conductive and piezoresistive polymer nanocomposites using multiwalled carbon nanotubes in a flexible copolyester: Spectroscopic, morphological, mechanical and electrical properties(Amsterdam [u.a.] : Elsevier, 2022) Dhakal, Kedar Nath; Khanal, Santosh; Krause, Beate; Lach, Ralf; Grellmann, Wolfgang; Le, Hai Hong; Das, Amit; Wießner, Sven; Heinrich, Gert; Pionteck, Jürgen; Adhikari, RameshwarNanocomposites of multiwalled carbon nanotubes (MWCNTs) with poly(butylene adipate-co-terephthalate) (PBAT), a flexible aromatic–aliphatic copolyester, were prepared by melt mixing followed by compression moulding to investigate their spectroscopic, morphological, mechanical and electrical properties. A comparison of the Fourier transform infrared (FTIR) spectra of the neat polymer matrix and the composites showed no difference, implying a physical mixing of the matrix and the filler. A morphological investigation revealed the formation of a continuous and interconnected MWCNT network embedded in the polymer matrix with partial agglomeration. Increasing Martens hardness and indentation modulus and decreasing maximum indentation depth with increasing filler concentration demonstrated the reinforcement of the polymer by the MWCNTs. A volume resistivity of 4.6 × 105 Ω cm of the materials was achieved by the incorporation of only 1 wt.-% of the MWCNTs, which confirmed a quite low percolation threshold (below 1 wt.-%) of the nanocomposites. The electrical volume resistivity of the flexible nanocomposites was achieved up to 1.6 × 102 Ω cm, depending on the filler content. The elongation at the break of the nanocomposites at 374% and the maximum relative resistance changes (ΔR/R0) of 20 and 200 at 0.9 and 7.5% strains, respectively, were recorded in the nanocomposites (3 wt.-% MWCNTs) within the estimated volume resistivity range. A cyclic strain experiment shows the most stable and reproducible ΔR/R0 values in the 2%–5% strain range. The electrical conductivity and piezoresistivity of the investigated nanocomposites in correlation with the mechanical properties and observed morphology make them applicable for low-strain deformation-sensing.
- ItemDevelopment of a polymer composite with high electrical conductivity and improved impact strength for the application as bipolar plate(Melville, NY : AIP, 2016) Hopmann, C.; Windeck, C.; Cohnen, A.; Onken, J.; Krause, Beate; Pötschke, Petra; Hickmann, T.Bipolar plates constitute the most important structural component in fuel cell stacks. Highly filled thermoplastic composites with high electrical conductivity obtain an increasing importance in the design of bipolar plates as alternative to conventional metallic systems. Thermoplastics (e.g. PP) have suitable properties such as a good processability, chemical resistance, light weight and low production costs. As thermoplastics have low electrical conductivities, conductive fillers have to be included in the matrix. A high content of such fillers (e.g. graphite) in excess of 80 wt.-% is necessary to achieve the desired electrical properties. However, materials with such high filler contents embrittle readily. The workability in injection and compression molding is difficult and the mechanical stability is insufficient in case of strain deformation. As consequence, material failure and an inacceptable amount of damaged goods can be observed during the processing. As no suitable thermoplastic system is available for better mechanical properties, the induction and dispersion of a rubber phase in the thermoplastic matrix can be used to increase the impact strength of the conductive composite. In this research work a ternary composite, based on PP as matrix, EPDM as impact modifier and synthetic graphite as conductive filler, was developed. The material was produced using a 26 mm co-rotating, intermeshing twin-screw extruder. The amounts of PP, EPDM and graphite were varied systematically and a process window was defined that enables improved impact strength and high electrical conductivity of the new material. The results indicate that impact strength can be enhanced by about 99 % with an EPDM content of 30 wt.-% in the PP matrix. The electrical conductivity decreases in a small range with increasing content of EPDM, but the conductivity is still excellent for producing bipolar plates.
- ItemPolymer - Carbon nanotube composites for thermoelectric applications(Melville, NY : AIP, 2017) Luo, J.; Krause, Beate; Pötschke, PetraThe thermoelectric (TE) performance of electrically conductive thermoplastic composites prepared by melt mixing was investigated. A cost effective widely used in industry polymer, namely polypropylene (PP), was chosen as the matrix to fabricate the composites. Singlewalled carbon nanotubes (SWCNTs), the amount (2 wt%) of which was selected to be above the electrical percolation threshold (< 0.2 wt%), were used to form an electrical conducting network. Besides as-produced SWCNTs plasma modified tubes were employed to study the influence of the functionalization on the morphology, dispersion and TE properties of the PP composites. In addition, melt processing conditions, e.g. temperature, rotation speed, and time during mixing in a small-scale compounder were varied. Furthermore, an ionic liquid (IL, 1-methyl-3-octylimidazolium tetrafluoroborate) was used as a processing additive during melt mixing, which was confirmed to improve the electrical conductivity of the composites. Simultaneous increase in the Seebeck coefficient up to a value of 64 μV/K was recorded, leading to a much better power factor of 0.26 μW/(m·K2) compared to composites without IL. This melt mixing strategy opens new avenues for solvent-free, large scale fabrication of polymer based TE materials.