3 results
Search Results
Now showing 1 - 3 of 3
- ItemOccurrence of Flux Jumps in MgB2 Bulk Magnets during Pulse-Field Magnetization(Bristol : IOP Publ., 2020) Sakai, N.; Oka, T.; Yamanaka, K.; Dadiel, L.; Oki, H.; Ogawa, J.; Fukui, S.; Scheiter, J.; Häßler, W.; Yokoyama, K; Noudem, J.; Miryala, M.; Murakami, M.The magnetic flux capturing of MgB2 bulk magnets made by spark plasma sintering process has been precisely investigated to clarify the mechanism of flux motions during the pulse-field magnetization processes. The field trapping ratio B T/B P was evaluated as a key parameter of field trapping ability which strongly relates to the heat generation due to the rapid flux motion in the samples. The time dependence of magnetic flux density revealed the actual flux motion which penetrated the samples. The trapped fields B T and field trapping ratios B T/B P of various samples were classified into three regions of 'no flux flow', 'fast flux flow' and 'flux jump' according to the generation of heat and its propagation. A flux jump was observed late at 280 ms from the beginning of PFM process, while the field penetration B P showed its peak at 10 ms. Considering the heat propagation speed, the long-delayed flux jump should be attributed to the macroscopic barriers against the heat propagation to the surface centre of bulk magnet. © Published under licence by IOP Publishing Ltd.
- ItemShielding Effect on Flux Trapping in Pulsed-Field Magnetizing for Mg-B Bulk Magnet(Bristol : IOP Publ., 2021) Oka, T.; Yamanaka, K.; Sudo, K.; Dadiel, L.; Ogawa, J.; Yokoyama, K.; Häßler, W.; Noudem, J.; Berger, K.; Sakai, N.; Miryala, M.; Murakami, M.MgB2 superconducting bulk materials are characterized as simple and uniform metallic compounds, and capable of trapping field of non-distorted conical shapes. Although pulsed-field magnetization technique (PFM) is expected to be a cheap and an easy way to activate them, the heat generation due to the magnetic flux motion causes serious degradation of captured fields. The authors precisely estimated the flux trapping property of the bulk samples, found that the flux-shielding effect closely attributed to the sample dimensions. The magnetic field capturing of Ti-5.0wt% sample reached the highest value of 0.76 T. The applied field which reached the centre of the sample surface shifted from 1.0 T to 1.2 T with increasing sample thickness from 3.67 mm to 5.80 mm. This means that the shielding effect was enhanced with increasing the sample thickness. Moreover, Ti-addition affected the frequency of flux jump happenings. The occurrence of flux jumps was suppressed in 5.0wt%Ti-added sample. This means that the heat capacity of the compounds was promoted by Ti addition.
- ItemPinning and trapped field in MgB2- and MT-YBaCuO bulk superconductors manufactured under pressure(Bristol : IOP Publ., 2016) Prikhna, T.; Eisterer, M.; Chaud, X.; Weber, H.W.; Habisreuther, T.; Moshchil, V.; Kozyrev, A.; Shapovalov, A.; Gawalek, W.; Wu, M.; Litzkendorf, D.; Goldacker, W.; Sokolovsky, V.; Shaternik, V.; Rabier, J.; Joulain, A.; Grechnev, G.; Boutko, V.; Gusev, A.; Shaternik, A.; Barvitskiy, P.The relevant pinning centers of Abrikosov vortices in MgB2-based materials are oxygen-enriched Mg-B-O inclusions or nanolayers and inclusions of MgBx (x>4) phases. The high critical current densities, jc, of 106 and 103A/cm2 at 1 and 8.5 T, respectively, at 20 K can be achieved in polycrystalline materials (prepared at 2 GPa) containing a large amount of admixed oxygen. Besides, oxygen can be incorporated into the MgB2 structure in small amounts (MgB1.5O0.5), which is supported by Auger studies and calculations of the DOS and the binding energy. The jc of melt textured YBa2Cu3O7-δ (or Y123)-based superconductors (MT-YBaCuO) depends not only on the perfectness of texture and the amount of oxygen in the Y123 structure, but also on the density of twins and micro-cracks formed during the oxygenation (due to shrinking of the c-lattice parameter). The density of twins and microcracks increases with the reduction of the distance between Y2BaCuO5 (Y211) inclusions in Y123. At 77 K jc=8·104 A/cm2 in self-field and jc=103 A/cm2 at 10 T were found in materials oxygenated at 16 MPa for 3 days with a density of twins of 22–35 per µm (thickness of the lamellae: 45-30 nm) and a density of micro-cracks of 200–280 per mm. Pinning can occur at the points of intersection between the Y123 twin planes and the Y211 inclusions. MTYBaCuO at 77 K can trap 1.4 T (38×38×17 mm, oxygenated at 0.1 MPa for 20 days) and 0.8 T (16 mm in diameter and 10 mm thick with 0.45 mm holes oxygenated at 10 MPa for 53 h). The sensitivity of MgB2 to magnetic field variations (flux jumps) complicates estimates of the trapped field. At 20 K 1.8 T was found for a block of 30 mm in diameter and a thickness of 7.5 mm and 1.5 T (if the magnetic field was increased at a rate of 0.1 T) for a ring with dimensions 24×18 mm and a thickness of 8 mm.