2021, Wang, Xiaowei, Xu, Kehui, Cui, Wendi, Yang, Xi, Maitz, Manfred F., Li, Wei, Li, Xiangyang, Chen, Jialong

The in-situ formation of silver nanoparticles (AgNPs) via dopamine-reduction of Ag+ has been widely utilized for titanium implants to introduce antibacterial properties. In previous studies, the preparation of AgNPs has focused on controlling the feeding concentrations, while the pH of the reaction solution was ignored. Herein, we systematically determined the influence of various pH (4, 7, 10) and Ag+ concentrations (0.01, 0.1 mg/mL) on the AgNPs formation, followed by the evaluation of the antibacterial properties in vitro and in vivo. The results revealed that an alkaline environment was favourable for AgNP formation and resulted in more particles. Although the AgNPs bearing Ti had lower biocompatibilities, it was significantly improved after 7 days of mineralization in simulated body fluid. The outstanding antibacterial property of the AgNPs was well maintained after one day and seven days of implantation. Moreover, 3D micro-CT modelling showed that the pH 10/0.1 group exhibited remarkable osteogenesis, which may be due to their strong antibacterial properties and ability to promote mineralization. Therefore, we have demonstrated that the solution pH was as important as the feeding Ag+ concentration in determining AgNP formation, and it has paved the way for developing various AgNP-loaded surfaces that could meet different antibacterial needs.

2023, Akman, Adnan, Alberta, Ludovico Andrea, Giraldo-Osorno, Paula Milena, Turner, Adam Benedict, Hantusch, Martin, Palmquist, Anders, Trobos, Margarita, Calin, Mariana, Gebert, Annett

Metastable Ti–Nb alloys are promising bone-implant materials due to improved mechanical biofunctionality and biocompatibility. To overcome increasing bacterial infection risk, alloying with antibacterial elements is a promising strategy. This study investigates the effect of minor gallium (Ga) additions (4, 8 wt% Ga) to as-cast and solution-treated β-type Ti–45Nb-based alloy (96(Ti–45Nb)-4Ga, 92(Ti–45Nb)-8Ga (wt.%)) on corrosion and passive film properties, as well as cytocompatibility and antibacterial activity. The electrochemical properties were evaluated by potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), and Mott-Schottky analyses in phosphate-buffered saline (PBS). X-ray photoelectron spectroscopy (XPS) was performed to analyze the chemical composition of passive films. Early adhesion and viability of macrophages and Staphylococcus aureus were assessed by nucleocounting and colony-forming unit counting, respectively. The results showed that high corrosion resistance and passive film properties of Ti–45Nb are retained and even slightly improved with Ga. EIS results revealed that Ga addition improves the passive film resistance. XPS measurements of 92(Ti–45Nb)-8Ga show that the passive film contains Ti-, Nb- and Ga-based oxides, implying the formation of mixed (Ti–Nb-Ga) oxides. In addition, marginal Ga ion release rate was detected under free corrosion conditions. Therefore, it can be assumed that Ga species may contribute to passive film formation on Ga-containing alloys. The 92(Ti–45Nb)-8Ga elicited an antibacterial effect against S. aureus compared to cp-Ti at 4 h. Moreover, Ga-containing alloys showed good cytocompatibility with THP-1 macrophages at 24 h. In conclusion, it was demonstrated that Ga additions to Ti–45Nb are beneficial to corrosion resistance and showed promising initial host and bacterial interactions.