Mechanical performance and corrosion behaviour of Zr-based bulk metallic glass produced by selective laser melting
2020, Deng, L., Gebert, A., Zhang, L., Chen, H.Y., Gu, D.D., Kühn, U., Zimmermann, M., Kosiba, K., Pauly, S.
Nearly fully dense, glassy Zr52.5Cu17.9Ni14.6Al10Ti5 bulk specimens were fabricated by selective laser melting (SLM) and their behaviour during compressive loading, during wear testing and in a corrosive medium was investigated. Their performance was compared with as-cast material of the same composition. The additively manufactured samples exhibit a yield strength around 1700 MPa combined with a plastic strain of about 0.5% after yielding despite the residual porosity of 1.3%, which is distributed uniformly in the samples. The propagation of shear bands in the bulk metallic glass prepared by SLM was studied. The specific wear rate and the worn surfaces demonstrated that similar wear mechanisms are active in the SLM and the as-cast samples. Hence, manufacturing the glass in layers does not adversely affect the wear properties. The same holds for the corrosion tests, which were carried out in 0.01 M Na2SO4 and 0.1 M NaCl electrolyte. The anodic polarization curves of SLM samples and as-cast samples revealed a similar corrosion behaviour. However, the SLM samples have a slightly reduced susceptibility to pitting corrosion and exhibit an improved surface healing ability, which might be attributed to an improved homogeneity of the additively manufactured glass.
Switchable double-sided micropatterned adhesives for selective fixation and detachment
2019, Tinnemann, V., Arzt, E., Hensel, R.
Micropatterned dry adhesives are promising candidates for the development of innovative adhesive platforms. Their reversible adhesion to various materials and surfaces has been reported over more than a decade. Switching between a strong and a weak adhesive state can be introduced by elastic buckling instabilities of the microstructure. In this work, we report on novel adhesive pads that exhibit micropatterned pillars on both sides. In double-sided PDMS micropatterns, the dimensions of the pillar structures were tuned by modulating the critical force for buckling during compressive loading. In this way, selective detachment of glass substrates was induced from one side of the pad. Our results indicate a significant switching efficiency of up to 83% between the strong and weak adhesive state. The new structures have high potential for emerging applications where temporary, double-sided fixations in combination with a predetermined detachment location are required. © 2018