    The effect of testing procedure on DSC measurements of Gd-Ti-Zr alloy using ZrO2 container
    (Bor : University of Belgrade, 2020) Turalska, P.; Homa, M.; Sobczak, N.; Gazda, A.; Wierzbicka-Miernik, A.; Kaban, I.
    Differential Scanning Calorimetry (DSC) was applied to determine the critical temperatures of phase transformations in the Gd40Ti30Zr30 alloy (wt%). The comparative measurements were carried out using three types of measuring devices at a temperature RT- 1650°C in the same flowing gas (Ar, 99.9992%) but applying different testing procedures, which allowed obtaining dissimilar oxygen contents in the surrounding atmosphere. The high temperature interaction and reactivity taking place between molten alloy samples and ZrO2 container during DSC tests were evaluated by structural analysis of the resulting interfaces using alloy samples solidified inside the ZrO2 containers. The conducted research has demonstrated methodological difficulties accompanying measurements of the thermophysical properties of Gd-rich alloys by the container-assisted DSC method, particularly when the tests are performed in flowing argon atmosphere with significantly reduced oxygen content. Under non-oxidizing conditions, the degradation of ZrO2 container can take place during DSC testing because the selected Gd40Ti30Zr30 alloy reacts with the ZrO2 to form a continuous interfacial reaction product layer. Under slightly oxidizing conditions, the gadolinium oxide formed in situ on the alloy surface, plays the role of a barrier for direct contact between molten alloy and container and thus may suppress or even prevent the degradation of the container and its subsequent strong bonding with the holder.
  • Thumbnail Image
    Item
    Linear and nonlinear relations between DSC parameters and elastic moduli for chemically and thermally treated human hair
    (Dordrecht [u.a.] : Springer Science + Business Media B.V, 2020) Wortmann, Franz J.; Wortmann, Gabriele; Popescu, Crisan
    Against the practical context of thermal straightening, hair samples were obtained with a chemical (bleaching) as well as a cumulative thermal history (0–800 s, 200 °C). On these samples, tensile testing and DSC analysis, both in the wet state, were conducted to obtain the elastic moduli Ew as well as denaturation temperatures TD and enthalpies ΔHD. 3D plots show overall linearity for the relationships between the parameters for natural hair. For bleached hair, pronounced nonlinearities develop beyond 300 s of thermal treatment. At this stage, TD as well as Ew approaches limiting values, consistent with the state of a highly cross-linked, thermoset polymer. 2D projections are used to investigate the correlations between pairs of parameters. The results show that bleaching imparts a specific sensitivity for thermal damage, namely, to the matrix proteins, which more readily than the intermediate filaments (IF) turn into a thermoset. Overall, correlations between parameters hold well prior to the thermoset range. It is thus suggested that tensile testing to determine the elastic modulus and DSC come to consistent and equivalent results, at least, for the current experimental context. However, while Ew combines contributions of IFs and matrix, DSC differentiates the specific property changes of these components. © 2019, The Author(s).