Influence of isothermal omega precipitation aging on deformation mechanisms and mechanical properties of a β-type Ti-Nb alloy
2022, Pilz, S., Hariharan, A., Günther, F., Zimmermann, M., Gebert, A.
In this study, the influence of ωiso precipitates on the active deformation mechanisms and the mechanical properties of the biomedical β-type Ti-40Nb alloy are revealed. Low temperature heat treatments (aging) at 573 K for durations up to 108.0 ks were carried out for a cold-rolled and recrystallized sample state. After an aging time of 3.6 ks the ωiso phase was determined by means of synchrotron XRD and the fraction and the crystallite size of ωiso increased progressively with increasing aging time. Due to the high intrinsic Young's modulus of the ωiso phase, the Young's modulus increased gradually with the aging time from 63 GPa, for the recrystallized reference condition, to values of 70 GPa (3.6 ks), 73 GPa (14.4 ks), 81 GPa (28.8 ks) and 96 GPa (108.0 ks). Depending on the aging time, also a change of the active deformation mechanisms occurred, resulting in significantly altered mechanical properties. For the single β-phase reference microstructure, stress-induced martensite (SIM) formation, {332} <113> twinning and dislocation slip were observed under tensile loading, resulting in a low 0.2% proof stress of around 315 MPa but a high elongation at fracture of 26.2%. With increasing aging time, SIM formation and mechanical twinning are progressively hindered under tensile loading. SIM formation could not be detected for samples aged longer than 3.6 ks. The amount and thickness of deformation twins is clearly reduced with increasing aging time and for samples aged longer than 14.4 ks deformation twinning is completely suppressed. As a result of the changed deformation mechanisms and the increase of the critical stress for slip caused by ωiso, the 0.2% proof stress of the aged samples increased gradually from 410 MPa (3.6 ks) to around 910 MPa (108.0 ks). With regard to application as new bone implant material, a balanced ratio of a low Young's modulus of E = 73 GPa and higher 0.2% proof stress of 640 MPa was achieved after an aging time of 14.4 ks.
Twinning phenomena along and beyond the bain path
2013, Kauffmann-Weiss, S., Kauffmann, A., Niemann, R., Freudenberger, J., Schultz, L., Fähler, S.
Twinning is a phenomenon that occurs, e.g., during deformation, martensitic transformation and film growth. The present study shows that the crystallography of twinning can be described by two twinning modes along the complete Bain transformation path and beyond connecting body-centered and face-centered cubic structures. To probe this concept, we used strained epitaxial films of the Fe-Pd magnetic shape memory system. As the substrate acts as an absolute reference frame, we could show by pole figure measurements that all observed twinning can be a body-centered and face-centered cubic twinning mode. This continuously transforms towards identity when approaching the complementary structure.