    Influence of microwave plasma treatment on the surface properties of carbon fibers and their adhesion in a polypropylene matrix
    (London [u.a.] : Institute of Physics, 2016) Scheffler, C.; Wölfel, E.; Förster, T.; Poitzsch, C.; Kotte, L.; Mäder, G.; Madsen, Bo; Biel, A.; Kusano, Y.; Lilholt, H.; Mikkelsen, L.P.; Mishnaevsky Jr., L.; Sørensen, B.F.
    A commercially available carbon fiber (CF) with an epoxy-based sizing (EP-sized CF) and an unsized CF have been plasma treated to study the effect on the fiber-matrix adhesion towards a polypropylene matrix. The EP-sized fiber was chosen because of its predictable low adhesion in a polypropylene (PP) matrix. The fibers have been modified using a microwave low-pressure O2/CO2/N2-gas plasma source (Cyrannus®) developed at IWS in a batch process. One aim of this study was the evaluation of parameters using high energies and short time periods in the plasma chamber to see the effect on mechanical performance of CF. These results will be the fundamental work for a planned continuous plasma modification line. The CF surface was characterized by determining the surface energies, single fiber tensile strength and XPS analysis. The adhesion behavior before and after plasma treatment was studied by single fiber pull-out test (SFPO) and scanning electron microscopy (SEM). It was shown that the CO2- and O2-plasma increases the number of functional groups on the fiber surface during short time plasma treatment of 30 s. Carboxylic groups on the unsized CF surface resulting from O2-plasma treatment lead to an enhanced fiber-matrix adhesion, whereas the fiber strength was merely reduced.
  • Thumbnail Image
    Item
    Surface, interphase and tensile properties of unsized, sized and heat treated basalt fibres
    (London [u.a.] : Institute of Physics, 2016) Förster, T.; Sommer, G.S.; Mäder, E.; Scheffler, C.
    Recycling of fibre reinforced polymers is in the focus of several investigations. Chemical and thermal treatments of composites are the common ways to separate the reinforcing fibres from the polymer matrices. However, most sizings on glass and basalt fibre are not designed to resist high temperatures. Hence, a heat treatment might also lead to a sizing removal, a decrease of mechanical performance and deterioration in fibre-matrix adhesion. Different basalt fibres were investigated using surface analysis methods as well as single fibre tensile tests and single fibre pull-out tests in order to reveal the possible causes of these issues. Heat treatment in air reduced the fibre tensile strength in the same level like heat treatment in nitrogen atmosphere, but it influenced the wetting capability. Re-sizing by a coupling agent slightly increased the adhesion strength and reflected a decreased post-debonding friction.
  • Thumbnail Image
    Item
    Mechanical performance and corrosion behaviour of Zr-based bulk metallic glass produced by selective laser melting
    (Amsterdam : Elsevier B.V., 2020) Deng, L.; Gebert, A.; Zhang, L.; Chen, H.Y.; Gu, D.D.; Kühn, U.; Zimmermann, M.; Kosiba, K.; Pauly, S.
    Nearly fully dense, glassy Zr52.5Cu17.9Ni14.6Al10Ti5 bulk specimens were fabricated by selective laser melting (SLM) and their behaviour during compressive loading, during wear testing and in a corrosive medium was investigated. Their performance was compared with as-cast material of the same composition. The additively manufactured samples exhibit a yield strength around 1700 MPa combined with a plastic strain of about 0.5% after yielding despite the residual porosity of 1.3%, which is distributed uniformly in the samples. The propagation of shear bands in the bulk metallic glass prepared by SLM was studied. The specific wear rate and the worn surfaces demonstrated that similar wear mechanisms are active in the SLM and the as-cast samples. Hence, manufacturing the glass in layers does not adversely affect the wear properties. The same holds for the corrosion tests, which were carried out in 0.01 M Na2SO4 and 0.1 M NaCl electrolyte. The anodic polarization curves of SLM samples and as-cast samples revealed a similar corrosion behaviour. However, the SLM samples have a slightly reduced susceptibility to pitting corrosion and exhibit an improved surface healing ability, which might be attributed to an improved homogeneity of the additively manufactured glass.