2021, Gabrysiak, Katharina, Gustmann, Tobias, Freudenberger, Jens, Neufeld, Kai, Giebeler, Lars, Leyens, Christoph, Kühn, Uta

Laser powder bed fusion (LPBF) can help to overcome two challenges occurring by casting of metastable Al alloys: (1) the high amount of casting defects and (2) the limited part size while maintaining rapid solidification of the whole cross-section. In this study, an Al92Mn6Ce2 alloy was processed crack-free without baseplate heating by LPBF. The high cooling rate during fabrication has a significant impact on the microstructure, which was characterized by SEM, TEM and XRD. The processing through LPBF causes a high amount and a strong refinement of the intermetallic Al20Mn2Ce precipitates. This leads, compared to suction-cast specimens, to a higher hardness (180 HV 5) and a higher tolerable compressive stress (>1200 MPa) associated with a pronounced plasticity without failure up to a strain of 40%. The extraordinary mechanical properties of additively manufactured Al92Mn6Ce2 can extend the possibilities of producing novel LPBF lightweight structures for potential applications under harsh conditions.