  • Item
    Influence of annealing on microstructure and mechanical properties of ultrafine-grained Ti45Nb
    (Amsterdam [u.a.] : Elsevier Science, 2019) Völker, B.; Maier-Kiener, V.; Werbach, K.; Müller, T.; Pilz, S.; Calin, M.; Eckert, J.; Hohenwarter, A.
    Beta-Ti alloys have been intensively investigated in the last years because of their favorable low Young's moduli, biocompatibility and bio-inertness, making these alloys interesting candidates for implant materials. Due to their low mechanical strength, efforts are currently devoted to increasing it. A promising way to improve the strength is to tailor the microstructure using severe plastic deformation (SPD). In this investigation high pressure torsion was used to refine the microstructure of a Ti-45wt.%Nb alloy inducing a grain size of ~50 nm. The main focus of the subsequent investigations was devoted to the thermal stability of the microstructure. Isochronal heat-treatments performed for 30 min in a temperature range up to 500 °C caused an increase of hardness with a peak value at 300 °C before the hardness decreased at higher temperatures. Simultaneously, a distinct temperature-dependent variation of the Young's modulus was also measured. Tensile tests revealed an increase in strength after annealing compared to the SPD-state. Microstructural investigations showed that annealing causes the formation of α-Ti. The findings suggest that the combination of severe plastic deformation with subsequent heat treatment provides a feasible way to improve the mechanical properties of SPD-deformed β-Ti alloys making them suitable for higher strength applications.
  • Item
    Synthesis and characterization of nanocrystallineMg-7.4%Al powders produced by mechanical alloying
    (Basel : MDPI AG, 2013) Chaubey, A.K.; Scudino, S.; Khoshkhoo, M.S.; Prashanth, K.G.; Mukhopadhyay, N.K.; Mishra, B.K.; Eckert, J.
    Nanocrystalline Mg-7.4%Al powder was prepared by mechanical alloying using a high-energy mill. The evolution of the various phases and their microstructure, including size and morphology of the powder particles in the course of milling and during subsequent annealing, were investigated in detail. Room temperature milling leads to a rather heterogeneous microstructure consisting of two distinct regions: Al-free Mg cores and Mg-Al intermixed areas. As a result, the material is mechanically heterogeneous with the Mg cores displaying low hardness (40–50 HV) and the Mg-Al intermixed regions showing high hardness of about 170 HV. The Mg cores disappear and the microstructure becomes (also mechanically) homogeneous after subsequent cryo-milling. Rietveld structure refinement reveals that the crystallite size of the milled powders decreases with increasing the milling time reaching a minimum value of about 30 nm. This is corroborated by transmission electron microscopy confirming an average grain size of ~25 nm.