2022, Riaz, Abdullah, Polley, Christian, Lund, Henrik, Springer, Armin, Seitz, Hermann

A critical-size bone defect in load-bearing areas is a challenging clinical problem in orthopaedic surgery. Titanium alloy (Ti6Al4V) scaffolds have advantages because of their biomechanical stability but lack electrical activity, which hinders their further use. This work is focused on the fabrication of Ti6Al4V-Barium Titanate (BaTiO3) bulk composite scaffolds to combine the biomechanical stability of Ti6Al4V with electrical activity through BaTiO3. For the first time, a hollow cylindrical Ti6Al4V is additively manufactured by electron beam melting and combined with piezoelectric BaTiO3 powder for joint processing in field-assisted sintering. Scanning electron microscope images on the interface of the Ti6Al4V-BaTiO3 composite scaffold showed that after sintering, the Ti6Al4V lattice structure bounded with BaTiO3 matrix without its major deformation. The Ti6Al4V-BaTiO3 scaffold had average piezoelectric constants of (0.63 ± 0.12) pC/N directly after sintering due to partial dipole alignment of the BaTiO3 tetragonal phase, which increased to (4.92 ± 0.75) pC/N after a successful corona poling. Moreover, the nanoindentation values of Ti6Al4V exhibited an average hardness and Young's modulus of (5.9 ± 0.9) GPa and (130 ± 14) GPa, and BaTiO3 showed (4.0 ± 0.6) GPa and (106 ± 10) GPa, respectively. It reveals that the Ti6Al4V is the harder and stiffer part in the Ti6Al4V-BaTiO3 composite scaffold. Such a scaffold has the potential to treat critical-size bone defects in load-bearing areas and guide tissue regeneration by physical stimulation.

2021, Riaz, Abdullah, Witte, Kerstin, Bodnar, Wiktor, Seitz, Hermann, Schell, Norbert, Springer, Armin, Burkel, Eberhard

CaTiO3 is a promising candidate as a pseudo-piezoelectric scaffold material for bone implantation. In this study, pure and magnesium/iron doped CaTiO3 are synthesized by sol-gel method and spark plasma sintering. Energy dispersive X-ray mapping confirm the homogenous distribution of doping elements in sintered samples. High-energy X-ray diffraction investigations reveal that doping of nanostructured CaTiO3 increased the strain and defects in the structure of CaTiO3 compared to the pure one. This led to a stronger pseudo-piezoelectric effect in the doped samples. The charge produced in magnesium doped CaTiO3 due to the direct piezoelectric effect is (2.9 ± 0.1) pC which was larger than the one produced in pure CaTiO3 (2.1 ± 0.3) pC, whereas the maximum charge was generated by iron doped CaTiO3 with (3.6 ± 0.2) pC. Therefore, the pseudo-piezoelectric behavior can be tuned by doping. This tuning of pseudo-piezoelectric response provides the possibility to systematically study the bone response using different piezoelectric strengths and possibly adjust for bone tissue engineering.