    Studies towards synthesis, evolution and alignment characteristics of dense, millimeter long multiwalled carbon nanotube arrays
    (Frankfurt, M. : Beilstein-Institut zur Förderung der Chemischen Wissenschaften, 2011) Mahanandia, P.; Schneider, J.J.; Engel, M.; Stühn, B.; Subramanyam, S.V.; Nanda, K.K.
    We report the synthesis of aligned arrays of millimeter long carbon nanotubes (CNTs), from benzene and ferrocene as the molecular precursor and catalyst respectively, by a one-step chemical vapor deposition technique. The length of the grown CNTs depends on the reaction temperature and increases from ~85 μm to ~1.4 mm when the synthesis temperature is raised from 650 to 1100°C, while the tube diameter is almost independent of the preparation temperature and is ~80 nm. The parallel arrangement of the CNTs, as well as their tube diameter can be verified spectroscopically by small angle X-ray scattering (SAXS) studies. Based on electron diffraction scattering (EDS) studies of the top and the base of the CNT films, a root growth process can be deduced.
  • Thumbnail Image
    Item
    Impact of synthesis temperature on morphology, rheology and electromagnetic interference shielding of CVD-grown carbon nanotube/polyvinylidene fluoride nanocomposites
    (Lausanne : Elsevier Sequoia, 2017) Mirkhani, Seyyed Alireza; Arjmand, Mohammad; Sadeghi, Soheil; Krause, Beate; Pötschke, Petra; Sundararaj, Uttandaraman
    Employing chemical vapor deposition technique, multi-walled carbon nanotubes (CNTs) were synthesized over Fe catalyst at a broad range of temperatures, i.e. 550° C to 950° C (at 100° C intervals). CNTs were melt-mixed into a polyvinylidene fluoride (PVDF) matrix at various loadings, and then compression molded. Surprisingly, despite the ascending trend of CNT powder conductivity with the synthesis temperature, the nanocomposites made with CNT synthesized at 650° C had significantly lower percolation threshold (around 0.4 wt%) and higher electromagnetic interference shielding effectiveness (EMI SE) (20.3 dB over the X-band for 3.5 wt% CNT and 1.1 mm thickness) than the other temperatures. Exhaustive characterization studies were conducted on both CNTs and composites to unveil their morphological and electrical characteristics. Superior EMI shielding of CNT650° C was attributed to a combination of high carbon purity, aspect ratio, crystallinity, and moderate powder conductivity along with decent state of dispersion within the PVDF matrix.